{"title":"Stress corrosion cracking susceptibility of a new nickel-based alloy in different environments","authors":"Zhenyu Chen, Zhongliang Zhu, Hasan I. Khan, Zhengzong Chen, Naiqiang Zhang","doi":"10.1002/maco.202314212","DOIUrl":null,"url":null,"abstract":"<p>Stress corrosion cracking (SCC) susceptibility of a new nickel-based alloy C-HRA-2 under two types of superheated steam (SHS) (0.1 and 8 MPa) and supercritical water (SCW) (25 MPa) at 650°C was studied through slow strain rate tensile tests at a strain rate of 5 × 10<sup>−7 </sup>s<sup>−1</sup>. The results indicate that C-HRA-2 exhibits SCC susceptibility in both SHS and SCW, and the susceptibility increases with increasing pressure. Transgranular fracture (located inside) characterized by dimples/micropores and intergranular fracture (located at the edge) characterized by rock-sugar-like morphology was observed in all specimens. The brittleness of the alloy increases with the increase of medium pressure. A large number of cracks perpendicular to the loading axis were noticed on the gauge surface. The SCC mechanism of C-HRA-2 under steam and SCW is dynamic embrittlement.</p>","PeriodicalId":18225,"journal":{"name":"Materials and Corrosion-werkstoffe Und Korrosion","volume":"75 8","pages":"965-977"},"PeriodicalIF":1.6000,"publicationDate":"2024-03-27","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials and Corrosion-werkstoffe Und Korrosion","FirstCategoryId":"88","ListUrlMain":"https://onlinelibrary.wiley.com/doi/10.1002/maco.202314212","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
Stress corrosion cracking (SCC) susceptibility of a new nickel-based alloy C-HRA-2 under two types of superheated steam (SHS) (0.1 and 8 MPa) and supercritical water (SCW) (25 MPa) at 650°C was studied through slow strain rate tensile tests at a strain rate of 5 × 10−7 s−1. The results indicate that C-HRA-2 exhibits SCC susceptibility in both SHS and SCW, and the susceptibility increases with increasing pressure. Transgranular fracture (located inside) characterized by dimples/micropores and intergranular fracture (located at the edge) characterized by rock-sugar-like morphology was observed in all specimens. The brittleness of the alloy increases with the increase of medium pressure. A large number of cracks perpendicular to the loading axis were noticed on the gauge surface. The SCC mechanism of C-HRA-2 under steam and SCW is dynamic embrittlement.
期刊介绍：
Materials and Corrosion is the leading European journal in its field, providing rapid and comprehensive coverage of the subject and specifically highlighting the increasing importance of corrosion research and prevention.
Several sections exclusive to Materials and Corrosion bring you closer to the current events in the field of corrosion research and add to the impact this journal can make on your work.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们