Erwin Abdul Rahim, Ahmad Ridhay, Sitti Nur Halizah, Indriani, Husain Sosidi, Khairuddin, N. I. Inda, Nurakhirawati, Moh. Mirzan, Aini Auliana Amar
{"title":"Sintesis dan Karakterisasi Polivinil Alkohol (PVA) Terlapis Polieugenol","authors":"Erwin Abdul Rahim, Ahmad Ridhay, Sitti Nur Halizah, Indriani, Husain Sosidi, Khairuddin, N. I. Inda, Nurakhirawati, Moh. Mirzan, Aini Auliana Amar","doi":"10.22487/kovalen.2024.v10.i1.17088","DOIUrl":null,"url":null,"abstract":"A study has been conducted on materials containing polyvinyl alcohol (PVA) coated with poly eugenol. This research aims to explore the synthesis process and properties of PVA coated with poly eugenol. Characterization of PVA includes tensile strength measurement and surface observation using SEM. Additionally, the antioxidant activity of PVA was also tested using the DPPH method. In this study, PVA films were obtained by dissolving PVA in a water solvent. The characterization results indicate that the tensile strength ranges from 25.56 to 271.10 Mpa, elongation reaches 315.20 to 320%, and the young modulus ranges from 4.05 to 6.27 Mpa. Surface observation with SEM shows a smooth surface without pores. The antioxidant activity test shows IC50 values ranging from 84.11 to 175.37 ppm.","PeriodicalId":17905,"journal":{"name":"KOVALEN: Jurnal Riset Kimia","volume":"16 31","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2024-05-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"KOVALEN: Jurnal Riset Kimia","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.22487/kovalen.2024.v10.i1.17088","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
A study has been conducted on materials containing polyvinyl alcohol (PVA) coated with poly eugenol. This research aims to explore the synthesis process and properties of PVA coated with poly eugenol. Characterization of PVA includes tensile strength measurement and surface observation using SEM. Additionally, the antioxidant activity of PVA was also tested using the DPPH method. In this study, PVA films were obtained by dissolving PVA in a water solvent. The characterization results indicate that the tensile strength ranges from 25.56 to 271.10 Mpa, elongation reaches 315.20 to 320%, and the young modulus ranges from 4.05 to 6.27 Mpa. Surface observation with SEM shows a smooth surface without pores. The antioxidant activity test shows IC50 values ranging from 84.11 to 175.37 ppm.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们