Determination of Ductile Tearing Resistance parameter of Interstitial-Free Steel Sheet

Procedia Structural Integrity Pub Date : 2024-01-01 DOI:10.1016/j.prostr.2024.05.042

S.K. Chandra , P.S. De , P.C. Chakraborti

{"title":"Determination of Ductile Tearing Resistance parameter of Interstitial-Free Steel Sheet","authors":"S.K. Chandra , P.S. De , P.C. Chakraborti","doi":"10.1016/j.prostr.2024.05.042","DOIUrl":null,"url":null,"abstract":"<div>The present work deals with the characterization of ductile tearing resistance of 1 mm thick interstitial free steel sheet using crack tip opening angle (φ), and δ5 concepts with some experimental modification. CTOA (φ) measurements on the specimen surface at the growing crack tip have been performed using light microscope on both pre-cracked DENT and SENT specimens at three ramp rates following the essence of ASTM E 2472. In order to determine the effect of pre-cracking, CTOA of the notched (ρ:0.1 mm) SENT specimen has also been measured at 10-4 s-1. The transferability of φ−Δα and δ5−Δα between two geometries has been verified. It is concluded that for a specified thickness both φ−Δα and δ5−Δα plots can be used for crack growth characterisation of sheet metals even without using pre-cracked specimens. However, the angle φ(δ5) determined from δ5−Δα curve is not the true measure of optical CTOA,φ as the δ5 gauge position does not follow the tip position of the growing crack.</div>","PeriodicalId":20518,"journal":{"name":"Procedia Structural Integrity","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2024-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S2452321624004712/pdf?md5=ab3c3c9512968b85b291f87e741a9baf&pid=1-s2.0-S2452321624004712-main.pdf","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Procedia Structural Integrity","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2452321624004712","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

The present work deals with the characterization of ductile tearing resistance of 1 mm thick interstitial free steel sheet using crack tip opening angle (φ), and δ₅ concepts with some experimental modification. CTOA (φ) measurements on the specimen surface at the growing crack tip have been performed using light microscope on both pre-cracked DENT and SENT specimens at three ramp rates following the essence of ASTM E 2472. In order to determine the effect of pre-cracking, CTOA of the notched (ρ:0.1 mm) SENT specimen has also been measured at 10^-4 s^-1. The transferability of φ−Δα and δ₅−Δα between two geometries has been verified. It is concluded that for a specified thickness both φ−Δα and δ₅−Δα plots can be used for crack growth characterisation of sheet metals even without using pre-cracked specimens. However, the angle φ(δ₅) determined from δ₅−Δα curve is not the true measure of optical CTOA,φ as the δ₅ gauge position does not follow the tip position of the growing crack.

查看原文

微信好友朋友圈 QQ好友复制链接

本刊更多论文

无间隙钢板韧性抗撕裂参数的测定

本研究采用裂纹尖端张开角 (φ)、δ5 和一些实验修正概念，对厚度为 1 毫米的无间隙钢板的韧性抗撕裂性能进行了表征。按照 ASTM E 2472 的精髓，在三种斜率下，使用光学显微镜对预开裂的 DENT 和 SENT 试样生长裂纹尖端的试样表面进行了 CTOA（φ）测量。为了确定预开裂的影响，还以 10-4 s-1 的速率测量了缺口（ρ:0.1 mm）SENT 试样的 CTOA。φ-Δα和δ5-Δα在两种几何形状之间的可转移性已得到验证。结论是，对于特定厚度，即使不使用预裂纹试样，φ-Δα 和 δ5-Δα 图也可用于表征金属板的裂纹生长。然而，根据 δ5-Δα 曲线确定的角度 φ(δ5) 并不是光学 CTOA,φ 的真实测量值，因为 δ5 量规的位置并不跟随裂纹生长的尖端位置。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

求助全文

约1分钟内获得全文去求助

来源期刊