Influence of Nb/V on the corrosion behavior of high-strength anti-seismic rebar in marine environments

IF 6.6 2区 材料科学 Q1 MATERIALS SCIENCE, MULTIDISCIPLINARY npj Materials Degradation Pub Date : 2024-07-22 DOI:10.1038/s41529-024-00493-3
Zeyun Zeng, Shangjun Gu, Jie Wang, Fulong Wei, Zhiying Li, Hui Yang, Changrong Li
{"title":"Influence of Nb/V on the corrosion behavior of high-strength anti-seismic rebar in marine environments","authors":"Zeyun Zeng, Shangjun Gu, Jie Wang, Fulong Wei, Zhiying Li, Hui Yang, Changrong Li","doi":"10.1038/s41529-024-00493-3","DOIUrl":null,"url":null,"abstract":"In this study, the immersion test, surface analysis, cross-section analysis, quantitative analysis and electrochemical analysis were used to study the influence of Nb/V on the corrosion behavior of high-strength anti-seismic rebar in marine environments. The corrosion results clarified that the addition of Nb/V improved the corrosion resistance of the rebar, thereby reducing the corrosion rate of the rebar and improving the stability of corrosion layers. Firstly, the addition of Nb/V promoted the transformation of unstable Fe oxyhydroxides to stable Fe oxyhydroxides in the surface corrosion layers of the rebar, thus increasing the α/(β + γ) ratio, corrosion potential and total impedance value. Secondly, the addition of Nb/V induced the formation of Nb oxides and V oxides in the surface corrosion layers of the rebar, and the existence of these oxides repaired the surface defects of corrosion layers, thus enhancing the corrosion resistance performance of surface corrosion layers of the rebar.","PeriodicalId":19270,"journal":{"name":"npj Materials Degradation","volume":null,"pages":null},"PeriodicalIF":6.6000,"publicationDate":"2024-07-22","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.nature.com/articles/s41529-024-00493-3.pdf","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"npj Materials Degradation","FirstCategoryId":"88","ListUrlMain":"https://www.nature.com/articles/s41529-024-00493-3","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

Abstract

In this study, the immersion test, surface analysis, cross-section analysis, quantitative analysis and electrochemical analysis were used to study the influence of Nb/V on the corrosion behavior of high-strength anti-seismic rebar in marine environments. The corrosion results clarified that the addition of Nb/V improved the corrosion resistance of the rebar, thereby reducing the corrosion rate of the rebar and improving the stability of corrosion layers. Firstly, the addition of Nb/V promoted the transformation of unstable Fe oxyhydroxides to stable Fe oxyhydroxides in the surface corrosion layers of the rebar, thus increasing the α/(β + γ) ratio, corrosion potential and total impedance value. Secondly, the addition of Nb/V induced the formation of Nb oxides and V oxides in the surface corrosion layers of the rebar, and the existence of these oxides repaired the surface defects of corrosion layers, thus enhancing the corrosion resistance performance of surface corrosion layers of the rebar.

Abstract Image

Abstract Image

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Nb/V 对海洋环境中高强度抗震钢筋腐蚀行为的影响
本研究采用浸泡试验、表面分析、截面分析、定量分析和电化学分析等方法,研究了 Nb/V 对海洋环境中高强度抗震钢筋腐蚀行为的影响。腐蚀结果表明,添加 Nb/V 提高了螺纹钢的耐腐蚀性,从而降低了螺纹钢的腐蚀速率,提高了腐蚀层的稳定性。首先,Nb/V 的添加促进了钢筋表面腐蚀层中不稳定的铁氧氢氧化物向稳定的铁氧氢氧化物转化,从而提高了 α/(β + γ)比值、腐蚀电位和总阻抗值。其次,Nb/V 的加入诱导了钢筋表面腐蚀层中 Nb 氧化物和 V 氧化物的形成,这些氧化物的存在修复了腐蚀层的表面缺陷,从而提高了钢筋表面腐蚀层的耐腐蚀性能。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
npj Materials Degradation
npj Materials Degradation MATERIALS SCIENCE, MULTIDISCIPLINARY-
CiteScore
7.80
自引率
7.80%
发文量
86
审稿时长
6 weeks
期刊介绍: npj Materials Degradation considers basic and applied research that explores all aspects of the degradation of metallic and non-metallic materials. The journal broadly defines ‘materials degradation’ as a reduction in the ability of a material to perform its task in-service as a result of environmental exposure. The journal covers a broad range of topics including but not limited to: -Degradation of metals, glasses, minerals, polymers, ceramics, cements and composites in natural and engineered environments, as a result of various stimuli -Computational and experimental studies of degradation mechanisms and kinetics -Characterization of degradation by traditional and emerging techniques -New approaches and technologies for enhancing resistance to degradation -Inspection and monitoring techniques for materials in-service, such as sensing technologies
期刊最新文献
Insights into the degradation mechanism of Fe-40Ni-15Co superalloy exposed to marine atmospheric and high-temperature conditions Lifetime prediction of epoxy coating using convolutional neural networks and post processing image recognition methods Film-forming amines as corrosion inhibitors: a state-of-the-art review The effect of variable humidity on corrosion fatigue of AA7085-T7451 with surface salt deposits Unveiling the mechanism behind irregular inclusions triggering no HIC cracks in steels
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1