Contribution to the Fracture Mechanics Characterization of Repair Welding of Thick-Walled Ductile Cast Iron Components

Abstract

For the spheroidal graphite cast iron materials, also known as ductile cast iron (DCI), EN-GJS-400-18-LT and EN-GJS-450-18, different welding procedures were examined for potential repair welding. A repair weld was performed on thick cast iron plates using the optimum procedure in each case. The weld was evaluated for all areas of the welded joint (weld metal, fusion line/heat-affected zone and base metal). In addition to the metallographic microstructural analysis, the characterization of the repair weld was carried out by means of hardness distribution measurements, static tensile testing and notched bar impact testing as well as fracture mechanics investigations under static and under cyclic loading in a wide load ratio range. On this basis, a generalized description of cyclic crack growth could be made according to the NASGRO® MODEL. NASGRO® is a fracture mechanics and fatigue crack growth software. In accordance with the possible operating conditions of repair-welded, thick-walled components, the static and impact tests were performed in the temperature range down to \(-\)40 \({}^{\circ }\text {C}\).