Synthesis and characterization of B-type carbonated hydroxyapatite materials: Effect of carbonate content on mechanical strength and in vitro degradation

Abstract

The current approach in bone tissue engineering requires resorbable biomaterials that enhance bone formation while maintaining sufficient mechanical stability. In this work, the influence of three levels of B-type carbonate substitution in hydroxyapatite lattice on mechanical strength and degradation rate is analyzed. The inverse aqueous route has been selected as a synthesis method of four powders with carbonate substitution between 4 and 6 wt.%. X-ray fluorescence (XRF), (C-S)-Analysis, FT-Infrared, X-ray diffraction, DTA-TG and TEM were used to investigate chemical composition, type of substitution, thermal behaviour, and morphology of the powders. Disc shaped specimens were processed by uniaxial pressing and sintering in argon/CO₂ flow. Maximum temperatures of thermal treatment between 750 and 850 °C were selected to obtain similar porosity levels for the different compositions. The highest carbonate substituted material (5.3 wt.%) presented higher compressive strength and dissolution rate than the other materials showing the beneficial effect of B-type substitution in hydroxyapatite materials for bone repair.