{"title":"Effect of multi-element synergistic addition on the microstructure evolution and performance enhancement of laser hot-wire cladded Fe-based alloy","authors":"","doi":"10.1016/j.ijpvp.2024.105321","DOIUrl":null,"url":null,"abstract":"<div><p>To satisfy the requirements of hardness and corrosion resistance for laser additive manufacturing of hydraulic supports, this study applied the synergistic addition of C, B, Cr, Ni, Nb and Mo elements in Fe-based alloys. The multi-phases, martensite + austenite + ferrite were designed. The microstructure, hardness and corrosion resistance of the coatings were analyzed. Increasing the C and B contents could significantly increase the hardness of the coatings, while the corrosion resistance was decreased. The corrosion resistance of the coatings was determined by the Cr contents. However, increasing the Cr contents to 20.0 wt % resulted in the ferrite structure with lower hardness (21 HRC). The coatings with 0.25 wt % C, 1.2 wt % B and 19.0 wt % Cr showed the optimal matching of hardness (56 HRC) and corrosion resistance (survived in neutral salt spray test≥300h). The resulted coatings were mainly consisted of dendritic structure. Fine lath martensite phase was dominant in the dendrite regions. The interdendritic regions were consisted of nano-sized intermetallics with a mixture of σ+Nb + FeNb + Cr<sub>2</sub>Nb+(Fe,Cr)<sub>2</sub>B + NbC compounds. These interdendritic regions (14.2 GPa) showed higher hardness than that of the dendritic regions (7.1 GPa). The high Cr contents with finer dendritic structures were the major mechanisms for the excellent combination of hardness and corrosion resistance. The precipitation and growth mechanisms of the interdendritic phases were elaborated. This work provides a valuable reference for laser hot-wire cladding to prepare Fe-based alloys with high hardness and excellent corrosion resistance.</p></div>","PeriodicalId":54946,"journal":{"name":"International Journal of Pressure Vessels and Piping","volume":null,"pages":null},"PeriodicalIF":3.0000,"publicationDate":"2024-09-11","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"International Journal of Pressure Vessels and Piping","FirstCategoryId":"5","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0308016124001984","RegionNum":2,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"ENGINEERING, MECHANICAL","Score":null,"Total":0}
引用次数: 0
Abstract
To satisfy the requirements of hardness and corrosion resistance for laser additive manufacturing of hydraulic supports, this study applied the synergistic addition of C, B, Cr, Ni, Nb and Mo elements in Fe-based alloys. The multi-phases, martensite + austenite + ferrite were designed. The microstructure, hardness and corrosion resistance of the coatings were analyzed. Increasing the C and B contents could significantly increase the hardness of the coatings, while the corrosion resistance was decreased. The corrosion resistance of the coatings was determined by the Cr contents. However, increasing the Cr contents to 20.0 wt % resulted in the ferrite structure with lower hardness (21 HRC). The coatings with 0.25 wt % C, 1.2 wt % B and 19.0 wt % Cr showed the optimal matching of hardness (56 HRC) and corrosion resistance (survived in neutral salt spray test≥300h). The resulted coatings were mainly consisted of dendritic structure. Fine lath martensite phase was dominant in the dendrite regions. The interdendritic regions were consisted of nano-sized intermetallics with a mixture of σ+Nb + FeNb + Cr2Nb+(Fe,Cr)2B + NbC compounds. These interdendritic regions (14.2 GPa) showed higher hardness than that of the dendritic regions (7.1 GPa). The high Cr contents with finer dendritic structures were the major mechanisms for the excellent combination of hardness and corrosion resistance. The precipitation and growth mechanisms of the interdendritic phases were elaborated. This work provides a valuable reference for laser hot-wire cladding to prepare Fe-based alloys with high hardness and excellent corrosion resistance.
期刊介绍：
Pressure vessel engineering technology is of importance in many branches of industry. This journal publishes the latest research results and related information on all its associated aspects, with particular emphasis on the structural integrity assessment, maintenance and life extension of pressurised process engineering plants.
The anticipated coverage of the International Journal of Pressure Vessels and Piping ranges from simple mass-produced pressure vessels to large custom-built vessels and tanks. Pressure vessels technology is a developing field, and contributions on the following topics will therefore be welcome:
• Pressure vessel engineering
• Structural integrity assessment
• Design methods
• Codes and standards
• Fabrication and welding
• Materials properties requirements
• Inspection and quality management
• Maintenance and life extension
• Ageing and environmental effects
• Life management
Of particular importance are papers covering aspects of significant practical application which could lead to major improvements in economy, reliability and useful life. While most accepted papers represent the results of original applied research, critical reviews of topical interest by world-leading experts will also appear from time to time.
International Journal of Pressure Vessels and Piping is indispensable reading for engineering professionals involved in the energy, petrochemicals, process plant, transport, aerospace and related industries; for manufacturers of pressure vessels and ancillary equipment; and for academics pursuing research in these areas.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们