Experimental review and accuracy of etchants used for phase analysis of SAF2507 Super Duplex Stainless Steel

Abstract

The mechanical and corrosion properties of duplex stainless steels (DSS) depend on the distribution of ferrite and austenite as well as the presence of secondary phases. It is therefore necessary to accurately determine both the distribution of the phases and their morphology. The aim of this research is to define a standard method for the determination of the volume fraction of the phases present in a SAF2507 SDSS by analysing images acquired by light microscope. To do this, the material is heat-treated at 850 °C for 5 min, 15 min, 30 min, 1h, 5h to stimulate the formation of the σ-phase. The metallographic etchant capable of maximising phase contrast is then identified. Micrographic analyses are performed using different reagents at different holding times and temperatures, in order to find the best combination. A standard procedure is then defined for the image analysis. The data obtained are processed to calculate the phase distribution. The results are compared with the quantitative analysis performed using X-ray diffraction as reference.