Revealing interfacial degradation of Bi2Te3-based micro thermoelectric device under current shocks

Abstract

Micro thermoelectric devices (micro-TEDs) offer great potential for IoT and electronic thermal management. However, they face challenges with reliability under high current densities. This study elucidates the failure mechanisms of Bi₂Te₃-based micro-TEDs subjected to current shocks. Experimental results indicate that at a high current density of 1800 A/cm², the internal resistance of micro-TEDs increased by 12.9 % to 2.034 Ω. This led to a 52.0 % decrease in maximum output power at a 20 K temperature difference, dropping to 1.53 mW. Additionally, as the frequency of ON/OFF current applied to micro-TED increases, the resistance growth rate jumped from 0.764 mΩ/h for slow power cycling to 2.328 mΩ/h for fast power cycling. This indicates that higher cycling frequencies exacerbate the degradation of the device. In-situ TEM analysis revealed that current-induced elemental diffusion and electrical stress release led to the formation of NiTe₂ nanoparticles and intergranular fractures within the Bi₂Te₃ materials. These results indicate that interfacial degradation and subsequent grain delamination are primary causes to micro-TED failure under current shocks. These findings underscore the significance of considering electrical stress in micro-TED design to enhance reliability and performance for high-power applications.