A.E. Yaedu , L. Volpe , A. Shaik , F. Long , K. Daub , F. Scenini , S.Y. Persaud
{"title":"Understanding preferential intergranular oxidation in alloy X-750 in 480 °C CO-CO2 environments at the nanoscale","authors":"A.E. Yaedu , L. Volpe , A. Shaik , F. Long , K. Daub , F. Scenini , S.Y. Persaud","doi":"10.1016/j.corsci.2024.112496","DOIUrl":null,"url":null,"abstract":"<div><div>Alloy X-750 was exposed to a 480 °C CO-CO<sub>2</sub> reducing gas mixture at an oxygen partial pressure below the NiO dissociation pressure. Post-exposure analytical transmission electron microscopy (ATEM) analysis confirmed the occurrence of preferential intergranular oxidation (PIO) and internal oxidation which resulted in the formation of Ni nodules. Thus, reducing CO-CO<sub>2</sub> mixtures can promote PIO in Alloy X-750, similar to Alloy 600 exposed to similar oxygen partial pressure but in H<sub>2</sub>-steam environment. In Alloy X-750, intergranular oxidation of Ti and Al were observed to occur prior to Cr oxidation, while the presence of intergranular Cr carbides hinders PIO penetration depth.</div></div>","PeriodicalId":290,"journal":{"name":"Corrosion Science","volume":"240 ","pages":"Article 112496"},"PeriodicalIF":7.4000,"publicationDate":"2024-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Corrosion Science","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0010938X24006917","RegionNum":1,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
Alloy X-750 was exposed to a 480 °C CO-CO2 reducing gas mixture at an oxygen partial pressure below the NiO dissociation pressure. Post-exposure analytical transmission electron microscopy (ATEM) analysis confirmed the occurrence of preferential intergranular oxidation (PIO) and internal oxidation which resulted in the formation of Ni nodules. Thus, reducing CO-CO2 mixtures can promote PIO in Alloy X-750, similar to Alloy 600 exposed to similar oxygen partial pressure but in H2-steam environment. In Alloy X-750, intergranular oxidation of Ti and Al were observed to occur prior to Cr oxidation, while the presence of intergranular Cr carbides hinders PIO penetration depth.
期刊介绍：
Corrosion occurrence and its practical control encompass a vast array of scientific knowledge. Corrosion Science endeavors to serve as the conduit for the exchange of ideas, developments, and research across all facets of this field, encompassing both metallic and non-metallic corrosion. The scope of this international journal is broad and inclusive. Published papers span from highly theoretical inquiries to essentially practical applications, covering diverse areas such as high-temperature oxidation, passivity, anodic oxidation, biochemical corrosion, stress corrosion cracking, and corrosion control mechanisms and methodologies.
This journal publishes original papers and critical reviews across the spectrum of pure and applied corrosion, material degradation, and surface science and engineering. It serves as a crucial link connecting metallurgists, materials scientists, and researchers investigating corrosion and degradation phenomena. Join us in advancing knowledge and understanding in the vital field of corrosion science.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们