Cross-Linked Polyimide Aerogels with Excellent Thermal and Mechanical Properties.

Abstract

With the increasing development of productivity, new materials that allow for the efficient use of energy are slowly becoming a sought-after goal, as well as a challenge that is currently being faced. For this reason, we have made aerogels as the target of our research and prepared different series (CLPI (1-5)) of cross-linked polyimide aerogels by mixing and cross-linking the heat-insulating cross-linking agent 1,3,5-tris(4-aminobenzylamino)benzene (TAB) with polyamic acid solution. We created a three-dimensional spatial organization by using vacuum freeze-drying and programmed high-temperature drying, then controlled the concentration of the polyamidate solution to investigate the concentration and TAB's influence on aerogel-related properties. Among them, the shrinkage is reduced from 40% in CLPI-1 to 28% in CLPI-5, and it also shows excellent mechanical characteristics, the highest compression strength (CLPI-5) reaches 0.81 MPa and specific modulus reaches 41.95 KN m/Kg. In addition, adding TAB improves the aerogel thermal resistance, T₅ in N₂ from PI-2 519 °C to CLPI-2 556 °C. The three-dimensional network-type structure of the aerogel shows an excellent thermal insulation effect, where the thermal conductivity can be as low as 24.4 mWm^-1 K^-1. Compared with some protective materials, cross-linked polyimide aerogel presents better flame-retardant properties, greatly improving the scope of its application in the industrial protection.