{"title":"Study on the fatigue properties of SPR-bonded aluminum-steel sheet joints","authors":"Yangyang Zhao, Xiao Shi, Wurong Wang, Xicheng Wei","doi":"10.1016/j.ijadhadh.2024.103864","DOIUrl":null,"url":null,"abstract":"<div><div>This study deals mainly with the influence of adhesive layer on the fatigue behavior and fretting of self-piercing riveted (SPR) joint joining differing thicknesses of AlSi10MnMg aluminum and DP590 steel sheets in lap shear geometry. Fatigue life, failure modes, crack propagation and fretting behaviors of the SPR and SPR-bonded joints were investigated and compared. The results showed that the static strength and fatigue life of SPR-bonded joints were significantly enhanced than that of SPR joints, but the fatigue failure mode of SPR-bonded and SPR joints differed. The SPR-bonded joints all failed in a rivet tail pull-out mode at all tested loads, which accompanied with small cracking in the aluminum sheet in contact with the rivet tail at lower test load. However, the failure mode of the SPR joints shifted from the aluminum sheet cracking to rivet tail pull-out as the fatigue test load increased. And during the aluminum sheet cracking failure, the fatigue crack originated from the faying interface of aluminum and steel sheet at the vicinity of the rivet shank and propagated along the width direction of aluminum sheet. Fretting wear analysis showed that the overall extent of fretting decreased and the location of fretting areas varied due to the adhesive bonding. Fretting of SPR joints mostly existed at the faying interface between aluminum and steel about 1.5 mm away from the rivet shank and resulted in fatigue crack initiation, while the fretting region of SPR-bonded joints shifted to the faying interface between rivet tail and aluminum sheet.</div></div>","PeriodicalId":13732,"journal":{"name":"International Journal of Adhesion and Adhesives","volume":"136 ","pages":"Article 103864"},"PeriodicalIF":3.2000,"publicationDate":"2024-10-22","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"International Journal of Adhesion and Adhesives","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S014374962400246X","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"ENGINEERING, CHEMICAL","Score":null,"Total":0}
引用次数: 0
Abstract
This study deals mainly with the influence of adhesive layer on the fatigue behavior and fretting of self-piercing riveted (SPR) joint joining differing thicknesses of AlSi10MnMg aluminum and DP590 steel sheets in lap shear geometry. Fatigue life, failure modes, crack propagation and fretting behaviors of the SPR and SPR-bonded joints were investigated and compared. The results showed that the static strength and fatigue life of SPR-bonded joints were significantly enhanced than that of SPR joints, but the fatigue failure mode of SPR-bonded and SPR joints differed. The SPR-bonded joints all failed in a rivet tail pull-out mode at all tested loads, which accompanied with small cracking in the aluminum sheet in contact with the rivet tail at lower test load. However, the failure mode of the SPR joints shifted from the aluminum sheet cracking to rivet tail pull-out as the fatigue test load increased. And during the aluminum sheet cracking failure, the fatigue crack originated from the faying interface of aluminum and steel sheet at the vicinity of the rivet shank and propagated along the width direction of aluminum sheet. Fretting wear analysis showed that the overall extent of fretting decreased and the location of fretting areas varied due to the adhesive bonding. Fretting of SPR joints mostly existed at the faying interface between aluminum and steel about 1.5 mm away from the rivet shank and resulted in fatigue crack initiation, while the fretting region of SPR-bonded joints shifted to the faying interface between rivet tail and aluminum sheet.
期刊介绍：
The International Journal of Adhesion and Adhesives draws together the many aspects of the science and technology of adhesive materials, from fundamental research and development work to industrial applications. Subject areas covered include: interfacial interactions, surface chemistry, methods of testing, accumulation of test data on physical and mechanical properties, environmental effects, new adhesive materials, sealants, design of bonded joints, and manufacturing technology.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们