{"title":"The effect of carbon black on degradation of pipe grade black polyethylene in high concentration chlorine dioxide solutions","authors":"Amirhosein Sarafpour, Gholamreza Pircheraghi","doi":"10.1016/j.polymdegradstab.2024.111031","DOIUrl":null,"url":null,"abstract":"<div><div>In this research, the impact of carbon black on the accelerated degradation of pipe grade polyethylene (PE100) exposed to high levels of chlorine dioxide (150 ppm) is examined. Tensile testing reveals a faster degradation rate in black samples compared to neat samples, indicating a detrimental effect of carbon black aggregates on the polymer's aging process. Rheological analysis shows changes in molecular weight and structure due to chemical degradation and chain scission and can be a reliable method for detecting slight changes in molecular structure. Isothermal crystallization shows a slowdown in crystallization kinetics at first, explained by gel-formation due to crosslinking which hinder the crystallization, and then an increase in the kinetics as apparently the chain scission gets dominant again. Neat samples exhibit a higher density of tie molecules, indirectly revealed by much more fibrils in crack wall observed in FESEM images, suggesting better resistance to chemical degradation while the black sample shows a much less fibrillar crack wake and becomes almost completely devoid of any fibrils at later stages of aging. The fibrils, which essentially offer a load-bearing role against the widening and growth of the crack play a key role in resistance to slow crack growth (SCG). Therefore, the higher SCG resistance is expected for neat grade compared to black samples. The study proposes a dual-layer pipe design with a UV-resistant black outer layer and an oxidation-resistant neat inner layer to prolong the lifespan of PE100 pipes by protecting against UV radiation and chemical reactions. This solution offers increased durability, lower maintenance costs, and environmental sustainability benefits.</div></div>","PeriodicalId":406,"journal":{"name":"Polymer Degradation and Stability","volume":"230 ","pages":"Article 111031"},"PeriodicalIF":6.3000,"publicationDate":"2024-10-12","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Polymer Degradation and Stability","FirstCategoryId":"92","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0141391024003744","RegionNum":2,"RegionCategory":"化学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"POLYMER SCIENCE","Score":null,"Total":0}
引用次数: 0
Abstract
In this research, the impact of carbon black on the accelerated degradation of pipe grade polyethylene (PE100) exposed to high levels of chlorine dioxide (150 ppm) is examined. Tensile testing reveals a faster degradation rate in black samples compared to neat samples, indicating a detrimental effect of carbon black aggregates on the polymer's aging process. Rheological analysis shows changes in molecular weight and structure due to chemical degradation and chain scission and can be a reliable method for detecting slight changes in molecular structure. Isothermal crystallization shows a slowdown in crystallization kinetics at first, explained by gel-formation due to crosslinking which hinder the crystallization, and then an increase in the kinetics as apparently the chain scission gets dominant again. Neat samples exhibit a higher density of tie molecules, indirectly revealed by much more fibrils in crack wall observed in FESEM images, suggesting better resistance to chemical degradation while the black sample shows a much less fibrillar crack wake and becomes almost completely devoid of any fibrils at later stages of aging. The fibrils, which essentially offer a load-bearing role against the widening and growth of the crack play a key role in resistance to slow crack growth (SCG). Therefore, the higher SCG resistance is expected for neat grade compared to black samples. The study proposes a dual-layer pipe design with a UV-resistant black outer layer and an oxidation-resistant neat inner layer to prolong the lifespan of PE100 pipes by protecting against UV radiation and chemical reactions. This solution offers increased durability, lower maintenance costs, and environmental sustainability benefits.
期刊介绍：
Polymer Degradation and Stability deals with the degradation reactions and their control which are a major preoccupation of practitioners of the many and diverse aspects of modern polymer technology.
Deteriorative reactions occur during processing, when polymers are subjected to heat, oxygen and mechanical stress, and during the useful life of the materials when oxygen and sunlight are the most important degradative agencies. In more specialised applications, degradation may be induced by high energy radiation, ozone, atmospheric pollutants, mechanical stress, biological action, hydrolysis and many other influences. The mechanisms of these reactions and stabilisation processes must be understood if the technology and application of polymers are to continue to advance. The reporting of investigations of this kind is therefore a major function of this journal.
However there are also new developments in polymer technology in which degradation processes find positive applications. For example, photodegradable plastics are now available, the recycling of polymeric products will become increasingly important, degradation and combustion studies are involved in the definition of the fire hazards which are associated with polymeric materials and the microelectronics industry is vitally dependent upon polymer degradation in the manufacture of its circuitry. Polymer properties may also be improved by processes like curing and grafting, the chemistry of which can be closely related to that which causes physical deterioration in other circumstances.