Evaluation of Microleakage of Orthograde Root-Filling Materials in Immature Permanent Teeth: An In Vitro Study.

IF 3 Q3 MATERIALS SCIENCE, BIOMATERIALS International Journal of Biomaterials Pub Date : 2024-10-29 eCollection Date: 2024-01-01 DOI:10.1155/2024/8867854
Upma Das, Vanita Gautam, Snigdha Shubham, Shristi Raut
{"title":"Evaluation of Microleakage of Orthograde Root-Filling Materials in Immature Permanent Teeth: An In Vitro Study.","authors":"Upma Das, Vanita Gautam, Snigdha Shubham, Shristi Raut","doi":"10.1155/2024/8867854","DOIUrl":null,"url":null,"abstract":"<p><p><b>Introduction:</b> The absence of a barrier in an open root apex makes endodontic treatment challenging as root-filling material can easily reach the surrounding tissue. The aim of the study was to compare the apical microleakage associated with mineral trioxide aggregate (MTA), biodentine, custom-made gutta-percha with MTA plus and custom-made gutta-percha with Adseal in immature permanent teeth by dye penetration method. <b>Methods:</b> Apical 2 mm of 60 single-rooted mandibular premolar teeth was resected to create divergent open apices and 10 teeth each were filled with Biodentine plug, MTA plug, custom-made gutta-percha with MTA plus sealer and custom-made gutta-percha with Adseal sealer. Ten teeth each acted as positive and negative controls. All the samples were stored at 37°C at 100% humidity for 5 weeks and then immersed in 2% Rhodamine B dye for 24 h. Transverse sectioning was done apically at 1 mm and 3 mm to evaluate dye penetration under a fluorescence microscope using ImageJ software. <b>Results:</b> There was a significantly greater microleakage at 1 mm cross section compared to 3 mm (<i>p</i> < 0.0001). At 1 mm cross section, the apical microleakage was the highest for the MTA plug with a mean leakage percentage of 48.08 ± 16.38, a mean depth of leakage of 0.46 ± 0.10 mm and a mean area of leakage of 1.35 ± 0.74 mm<sup>2</sup>, compared to other groups, and the difference was statistically significant. However, at a 3 mm cross section, MTA plus sealer with gutta-percha demonstrated the highest mean leakage percentage (25.01 ± 7.77) compared to other groups and the difference was statistically significant (<i>p</i> = 0.03). <b>Conclusion:</b> It can be concluded that the 3-mm-thick apical plug provided better sealing of the open apex compared to the 1 mm apical plug and there was no significant difference in microleakage among the Biodentine plug, MTA plug and Adseal sealer with gutta-percha plug at 3 mm cross section.</p>","PeriodicalId":13704,"journal":{"name":"International Journal of Biomaterials","volume":null,"pages":null},"PeriodicalIF":3.0000,"publicationDate":"2024-10-29","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.ncbi.nlm.nih.gov/pmc/articles/PMC11537741/pdf/","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"International Journal of Biomaterials","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1155/2024/8867854","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"2024/1/1 0:00:00","PubModel":"eCollection","JCR":"Q3","JCRName":"MATERIALS SCIENCE, BIOMATERIALS","Score":null,"Total":0}
引用次数: 0

Abstract

Introduction: The absence of a barrier in an open root apex makes endodontic treatment challenging as root-filling material can easily reach the surrounding tissue. The aim of the study was to compare the apical microleakage associated with mineral trioxide aggregate (MTA), biodentine, custom-made gutta-percha with MTA plus and custom-made gutta-percha with Adseal in immature permanent teeth by dye penetration method. Methods: Apical 2 mm of 60 single-rooted mandibular premolar teeth was resected to create divergent open apices and 10 teeth each were filled with Biodentine plug, MTA plug, custom-made gutta-percha with MTA plus sealer and custom-made gutta-percha with Adseal sealer. Ten teeth each acted as positive and negative controls. All the samples were stored at 37°C at 100% humidity for 5 weeks and then immersed in 2% Rhodamine B dye for 24 h. Transverse sectioning was done apically at 1 mm and 3 mm to evaluate dye penetration under a fluorescence microscope using ImageJ software. Results: There was a significantly greater microleakage at 1 mm cross section compared to 3 mm (p < 0.0001). At 1 mm cross section, the apical microleakage was the highest for the MTA plug with a mean leakage percentage of 48.08 ± 16.38, a mean depth of leakage of 0.46 ± 0.10 mm and a mean area of leakage of 1.35 ± 0.74 mm2, compared to other groups, and the difference was statistically significant. However, at a 3 mm cross section, MTA plus sealer with gutta-percha demonstrated the highest mean leakage percentage (25.01 ± 7.77) compared to other groups and the difference was statistically significant (p = 0.03). Conclusion: It can be concluded that the 3-mm-thick apical plug provided better sealing of the open apex compared to the 1 mm apical plug and there was no significant difference in microleakage among the Biodentine plug, MTA plug and Adseal sealer with gutta-percha plug at 3 mm cross section.

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
评估未成熟恒牙正交根充材料的微渗漏:体外研究
导言:开放的根尖没有屏障,使得根管治疗具有挑战性,因为根充材料很容易到达周围组织。本研究的目的是通过染料渗透法,比较未成熟恒牙中与三氧化二铝矿物质骨料(MTA)、生物碱、定制的古塔波瓷加 MTA 和定制的古塔波瓷加 Adseal 相关的根尖微渗漏情况。方法:切除 60 颗单根下颌前磨牙的根尖 2 毫米,形成分叉开放的根尖,并分别用 Biodentine 栓塞、MTA 栓塞、定制的带有 MTA plus 封闭剂的古塔波查和定制的带有 Adseal 封闭剂的古塔波查填充各 10 颗牙齿。阳性和阴性对照组各 10 颗牙齿。使用 ImageJ 软件在荧光显微镜下评估染料的渗透情况。结果:与 3 毫米横切面相比,1 毫米横切面的微渗漏率明显更高(p < 0.0001)。与其他组相比,在 1 毫米横截面上,MTA 插塞的顶端微渗漏最高,平均渗漏百分比为 48.08 ± 16.38,平均渗漏深度为 0.46 ± 0.10 毫米,平均渗漏面积为 1.35 ± 0.74 平方毫米,差异具有统计学意义。然而,在 3 毫米的横截面上,与其他组别相比,MTA 加带古塔漆的封闭剂的平均渗漏百分比(25.01 ± 7.77)最高,差异有统计学意义(p = 0.03)。结论可以得出结论,与 1 毫米的根尖塞相比,3 毫米厚的根尖塞能更好地密封开放的根尖,而且在 3 毫米横截面上,Biodentine 塞、MTA 塞和 Adseal 密封剂加古塔碱塞在微渗漏方面没有显著差异。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
International Journal of Biomaterials
International Journal of Biomaterials MATERIALS SCIENCE, BIOMATERIALS-
CiteScore
4.30
自引率
3.20%
发文量
50
审稿时长
21 weeks
期刊最新文献
Evaluation of Microleakage of Orthograde Root-Filling Materials in Immature Permanent Teeth: An In Vitro Study. Production of Composite Briquette Fuel from Brewery Wastewater Sludge and Spent Grains. Unveiling SmearOFF Efficacy in Smear Layer Removal through Ultrasonic Activation Examined by Scanning Electron Microscopy. Corrigendum to "New Nanosized V(III), Fe(III), and Ni(II) Complexes Comprising Schiff Base and 2-Amino-4-Methyl Pyrimidine: Synthesis, Properties, and Biological Activity". Effects of Various Decellularization Methods for the Development of Decellularized Extracellular Matrix from Tilapia (Oreochromis niloticus) Viscera.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1