Study on the effect of stress redistribution in different notched specimens of DD6 on the life of combined high and low cycle fatigue under high temperature

Abstract

Under combined high and low cycle fatigue (CCF) loading, the multi-axial stress state induced by geometric discontinuities of different notch forms under the same stress amplitude can result in significant differences in fatigue performance of DD6 alloy. Therefore, it is of great importance to study the CCF behavior of Ni-base single-crystal alloy samples with differing notch geometries at the high temperatures. In order to obtain an approximate CCF lifespan, different stress amplitudes need to be applied to DD6 specimens with different notch forms. In this study, two kinds of notched DD6 plate specimens with [001] orientation were studied by CCF test at 760 °C, and the amplitudes of stresses were acquired under the same service life level. The effect of stress redistribution, in particular stress triaxiality, was evaluated on CCF lifetime of the DD6 specimens. A damage model with anisotropy considering stress triaxiality effect was suggested. The results indicated that the conventional stress–strain variables could not reflect the trend of CCF lifetime for different geometrical notched DD6 specimens, whereas the stress triaxiality at the CCF load peak could. A modified Basquin model was introduced for predicting CCF life according to the stress triaxiality at the peak loading. It can accurately and efficiently estimate the CCF life of two kinds of notched DD6 plate specimens, and the life prediction results fall within a scatter band of ±3 times of fatigue life.