Junliang Xue , Wei Guo , Mingsheng Xia , Caiwang Tan , Jiaxin Shi , Yongxin Zhang , Zhandong Wan , Yulong Li , Hongqiang Zhang
{"title":"In-situ precipitation of carbides significantly enhances the hydrogen embrittlement resistance of advanced high-strength steels welded joints","authors":"Junliang Xue , Wei Guo , Mingsheng Xia , Caiwang Tan , Jiaxin Shi , Yongxin Zhang , Zhandong Wan , Yulong Li , Hongqiang Zhang","doi":"10.1016/j.corsci.2025.112697","DOIUrl":null,"url":null,"abstract":"<div><div>This study employed the laser <em>in-situ</em> post-weld heat treatment process to achieve <em>in-situ</em> precipitation of carbides (IPC) in the hydrogen embrittlement (HE) sensitive zone of QP980 steels laser welded joints. In the original joint with hydrogen pre-charging, cleavage fracture occurred at the inter-critical heat affected zone (ICHAZ). The IPC process only caused carbides to precipitate in martensite of the ICHAZ. The IPC joint with hydrogen pre-charging (5 min) exhibited ductile fracture at the base material during the slow strain rate tensile test, and the total elongation HE sensitivity of the joint was reduced from 84.6 % to 13.7 %.</div></div>","PeriodicalId":290,"journal":{"name":"Corrosion Science","volume":"245 ","pages":"Article 112697"},"PeriodicalIF":7.4000,"publicationDate":"2025-04-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Corrosion Science","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0010938X25000241","RegionNum":1,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"2025/1/9 0:00:00","PubModel":"Epub","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
This study employed the laser in-situ post-weld heat treatment process to achieve in-situ precipitation of carbides (IPC) in the hydrogen embrittlement (HE) sensitive zone of QP980 steels laser welded joints. In the original joint with hydrogen pre-charging, cleavage fracture occurred at the inter-critical heat affected zone (ICHAZ). The IPC process only caused carbides to precipitate in martensite of the ICHAZ. The IPC joint with hydrogen pre-charging (5 min) exhibited ductile fracture at the base material during the slow strain rate tensile test, and the total elongation HE sensitivity of the joint was reduced from 84.6 % to 13.7 %.
期刊介绍：
Corrosion occurrence and its practical control encompass a vast array of scientific knowledge. Corrosion Science endeavors to serve as the conduit for the exchange of ideas, developments, and research across all facets of this field, encompassing both metallic and non-metallic corrosion. The scope of this international journal is broad and inclusive. Published papers span from highly theoretical inquiries to essentially practical applications, covering diverse areas such as high-temperature oxidation, passivity, anodic oxidation, biochemical corrosion, stress corrosion cracking, and corrosion control mechanisms and methodologies.
This journal publishes original papers and critical reviews across the spectrum of pure and applied corrosion, material degradation, and surface science and engineering. It serves as a crucial link connecting metallurgists, materials scientists, and researchers investigating corrosion and degradation phenomena. Join us in advancing knowledge and understanding in the vital field of corrosion science.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们