Xiaoli Li , Litao Chang , Wenjun Liang , Chengpeng Liu , Zhijun Li , Yumiao Wang , Bin Leng
{"title":"Creep deformation and fracture of Ni-based alloy GH3535 in molten FLiNaK and Ar environment","authors":"Xiaoli Li , Litao Chang , Wenjun Liang , Chengpeng Liu , Zhijun Li , Yumiao Wang , Bin Leng","doi":"10.1016/j.corsci.2025.112902","DOIUrl":null,"url":null,"abstract":"<div><div>The creep deformation and fracture behavior of GH3535 alloy under varying stresses (190–270 MPa) in 700 °C molten FLiNaK salt and argon environments were systematically investigated. Under each experimental stress, specimens in molten FLiNaK salt exhibit lower fracture life and elongation compared to those in argon, with the disparity becoming more pronounced as the applied stress decreases. The alloy show a combination of ductile overload failure and intergranular fracture in both environments, whereas intergranular fracture is more pronounced in the molten salt environment. Notably, crack density and depth are greater in the molten salt environment due to its corrosive nature.</div></div>","PeriodicalId":290,"journal":{"name":"Corrosion Science","volume":"250 ","pages":"Article 112902"},"PeriodicalIF":7.4000,"publicationDate":"2025-07-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Corrosion Science","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0010938X2500229X","RegionNum":1,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"2025/3/31 0:00:00","PubModel":"Epub","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
The creep deformation and fracture behavior of GH3535 alloy under varying stresses (190–270 MPa) in 700 °C molten FLiNaK salt and argon environments were systematically investigated. Under each experimental stress, specimens in molten FLiNaK salt exhibit lower fracture life and elongation compared to those in argon, with the disparity becoming more pronounced as the applied stress decreases. The alloy show a combination of ductile overload failure and intergranular fracture in both environments, whereas intergranular fracture is more pronounced in the molten salt environment. Notably, crack density and depth are greater in the molten salt environment due to its corrosive nature.
期刊介绍：
Corrosion occurrence and its practical control encompass a vast array of scientific knowledge. Corrosion Science endeavors to serve as the conduit for the exchange of ideas, developments, and research across all facets of this field, encompassing both metallic and non-metallic corrosion. The scope of this international journal is broad and inclusive. Published papers span from highly theoretical inquiries to essentially practical applications, covering diverse areas such as high-temperature oxidation, passivity, anodic oxidation, biochemical corrosion, stress corrosion cracking, and corrosion control mechanisms and methodologies.
This journal publishes original papers and critical reviews across the spectrum of pure and applied corrosion, material degradation, and surface science and engineering. It serves as a crucial link connecting metallurgists, materials scientists, and researchers investigating corrosion and degradation phenomena. Join us in advancing knowledge and understanding in the vital field of corrosion science.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们