V. Opini, J. B. Fogagnolo, V. A. Borrás, R. Caram, J. Soyama
{"title":"Powder metallurgy processing of Nb-modified near β titanium alloys prepared with elemental powders","authors":"V. Opini, J. B. Fogagnolo, V. A. Borrás, R. Caram, J. Soyama","doi":"10.1080/00325899.2023.2228093","DOIUrl":null,"url":null,"abstract":"ABSTRACT Near β Ti alloys typically show high specific strength and provide a wide spectrum of mechanical properties with different heat treatments. In this work, a commercial near β Ti alloy Ti-5553 (Ti-5Al-5V-5Mo-3Cr-0.5Fe) was prepared through powder metallurgy using the blended elemental powder approach. Additionally, alloy modifications with 6 wt.% Nb (Ti-6Nb-5Al-2.5V-5Mo-3Cr-0.5Fe) and 12 wt.% Nb (Ti-12Nb-5Al-5Mo-3Cr-0.5Fe) were investigated. Specimens were prepared by uniaxial cold compaction of blended powders at room temperature with sintering conducted at 1300°C for 2 h under Ar atmosphere. Microstructure investigation revealed reasonable homogenisation of alloying elements and colony sizes in the order of 80-100 μm with porosity below 10%. Moreover, the bending strength of as-sintered Ti-12Nb-5Al-5Mo-3Cr-0.5Fe was about 850 MPa and the micro-Vickers hardness was approximately 370 HV. The alloy modifications with Nb increased strength without loss in flexural strain.","PeriodicalId":20392,"journal":{"name":"Powder Metallurgy","volume":null,"pages":null},"PeriodicalIF":1.9000,"publicationDate":"2023-06-26","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Powder Metallurgy","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/00325899.2023.2228093","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 0
Abstract
ABSTRACT Near β Ti alloys typically show high specific strength and provide a wide spectrum of mechanical properties with different heat treatments. In this work, a commercial near β Ti alloy Ti-5553 (Ti-5Al-5V-5Mo-3Cr-0.5Fe) was prepared through powder metallurgy using the blended elemental powder approach. Additionally, alloy modifications with 6 wt.% Nb (Ti-6Nb-5Al-2.5V-5Mo-3Cr-0.5Fe) and 12 wt.% Nb (Ti-12Nb-5Al-5Mo-3Cr-0.5Fe) were investigated. Specimens were prepared by uniaxial cold compaction of blended powders at room temperature with sintering conducted at 1300°C for 2 h under Ar atmosphere. Microstructure investigation revealed reasonable homogenisation of alloying elements and colony sizes in the order of 80-100 μm with porosity below 10%. Moreover, the bending strength of as-sintered Ti-12Nb-5Al-5Mo-3Cr-0.5Fe was about 850 MPa and the micro-Vickers hardness was approximately 370 HV. The alloy modifications with Nb increased strength without loss in flexural strain.
期刊介绍：
Powder Metallurgy is an international journal publishing peer-reviewed original research on the science and practice of powder metallurgy and particulate technology. Coverage includes metallic particulate materials, PM tool materials, hard materials, composites, and novel powder based materials.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们