{"title":"Failure analysis of type 304 stainless steel amine exchanger sheets in a gas sweetening plant","authors":"H. Panahi , A. Eslami , M.A. Golozar , A. Ashrafi Laleh , M. Aryanpur , M. Mazarei","doi":"10.1016/j.csefa.2017.08.002","DOIUrl":null,"url":null,"abstract":"<div><p>Amine exchangers are widely used in gas sweetening plants for amine solution regeneration process. This study is investigates cracking and leakage of a 304 type stainless steel plate in an amine exchanger unit, used between absorption and stripper towers. In this regard, micro and macro examinations were performed on the plate, and solution was analyzed. Micro cracks were observed on both sides of the plate, especially under the gasket region of the plate. Results showed that the main reason of cracking was intergranular corrosion accompanied by stress. High concentration of Formate in amine solution, and also high level of stress under gasket region, had initiated the intergranular corrosion and cracking.</p></div>","PeriodicalId":91224,"journal":{"name":"Case studies in engineering failure analysis","volume":"9 ","pages":"Pages 87-98"},"PeriodicalIF":0.0000,"publicationDate":"2017-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1016/j.csefa.2017.08.002","citationCount":"8","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Case studies in engineering failure analysis","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2213290217300500","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 8
Abstract
Amine exchangers are widely used in gas sweetening plants for amine solution regeneration process. This study is investigates cracking and leakage of a 304 type stainless steel plate in an amine exchanger unit, used between absorption and stripper towers. In this regard, micro and macro examinations were performed on the plate, and solution was analyzed. Micro cracks were observed on both sides of the plate, especially under the gasket region of the plate. Results showed that the main reason of cracking was intergranular corrosion accompanied by stress. High concentration of Formate in amine solution, and also high level of stress under gasket region, had initiated the intergranular corrosion and cracking.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们