Zheng Huang, Xingquan Jiang, Du-xin Li, Zhongchen Yang, Renwei Lu
{"title":"Effect of sintering temperature on microstructure and properties of MIM420 stainless steel","authors":"Zheng Huang, Xingquan Jiang, Du-xin Li, Zhongchen Yang, Renwei Lu","doi":"10.1080/00325899.2021.2006932","DOIUrl":null,"url":null,"abstract":"ABSTRACT This paper investigates the effect of different sintering temperatures on the microstructure and mechanical properties of 420 stainless steel prepared by metal injection molding (MIM). The results show that in the temperature range of 1300 to 1360, the internal structure of MIM420 stainless steel is mainly lath martensite and the fracture mode is quasi cleavage fracture. With the increase of sintering temperature, the relative density, strength and hardness of MIM420 stainless steel increase, and the carbon and oxygen content decreases, but the strength decreases when the sintering temperature exceeds 1340. When the sintering temperature reaches 1360, the sample will be slightly over sintered, so the appropriate sintering temperature is 1340. At 1340, the relative density, hardness, bending strength and ultimate tensile strength of the sample are 98.2 ± 0.4%, 54 ± 1HRC, 1229 ± 28 MPa and 1111 ± 26 MPa respectively.","PeriodicalId":20392,"journal":{"name":"Powder Metallurgy","volume":"65 1","pages":"214 - 221"},"PeriodicalIF":1.9000,"publicationDate":"2021-11-24","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"2","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Powder Metallurgy","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/00325899.2021.2006932","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 2
Abstract
ABSTRACT This paper investigates the effect of different sintering temperatures on the microstructure and mechanical properties of 420 stainless steel prepared by metal injection molding (MIM). The results show that in the temperature range of 1300 to 1360, the internal structure of MIM420 stainless steel is mainly lath martensite and the fracture mode is quasi cleavage fracture. With the increase of sintering temperature, the relative density, strength and hardness of MIM420 stainless steel increase, and the carbon and oxygen content decreases, but the strength decreases when the sintering temperature exceeds 1340. When the sintering temperature reaches 1360, the sample will be slightly over sintered, so the appropriate sintering temperature is 1340. At 1340, the relative density, hardness, bending strength and ultimate tensile strength of the sample are 98.2 ± 0.4%, 54 ± 1HRC, 1229 ± 28 MPa and 1111 ± 26 MPa respectively.
期刊介绍：
Powder Metallurgy is an international journal publishing peer-reviewed original research on the science and practice of powder metallurgy and particulate technology. Coverage includes metallic particulate materials, PM tool materials, hard materials, composites, and novel powder based materials.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们