L. Khademibami, Keith B. Ward, R. D. Seale, R. Shmulsky, J. Ratcliff
{"title":"Flexural Properties of Three-Ply Bolt-Laminated Pine Mats","authors":"L. Khademibami, Keith B. Ward, R. D. Seale, R. Shmulsky, J. Ratcliff","doi":"10.13073/fpj-d-22-00075","DOIUrl":null,"url":null,"abstract":"\n In the current study, three-ply bolt-laminated southern pine (Pinus sp.) 244 by 427 cm (8 by 14 ft) mats were evaluated. Mats were destructively tested in ⅓-point bending on a universal testing machine according to ASTM International standards. Twenty-eight unique specimens were destructively tested, and mean modulus of rupture (MOR) and modulus of elasticity (MOE) were calculated. According to the results both MOR and MOE values for the specimens were highly uniform. The mean MOR was 11.74 MPa (1,704 psi) and the mean MOE was 1,144 MPa (0.166 × 106 psi). Additionally, the values of parametric and nonparametric Fb (design fiber stress in bending values ) were reported as 4.05 MPa and 4.54 MPa (588 psi and 659 psi), respectively. The mechanical properties of these three-ply pine mats were also compared with other studies of mats from other species groups and design architectures.","PeriodicalId":12387,"journal":{"name":"Forest Products Journal","volume":null,"pages":null},"PeriodicalIF":1.1000,"publicationDate":"2023-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Forest Products Journal","FirstCategoryId":"97","ListUrlMain":"https://doi.org/10.13073/fpj-d-22-00075","RegionNum":4,"RegionCategory":"农林科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"FORESTRY","Score":null,"Total":0}
引用次数: 0
Abstract
In the current study, three-ply bolt-laminated southern pine (Pinus sp.) 244 by 427 cm (8 by 14 ft) mats were evaluated. Mats were destructively tested in ⅓-point bending on a universal testing machine according to ASTM International standards. Twenty-eight unique specimens were destructively tested, and mean modulus of rupture (MOR) and modulus of elasticity (MOE) were calculated. According to the results both MOR and MOE values for the specimens were highly uniform. The mean MOR was 11.74 MPa (1,704 psi) and the mean MOE was 1,144 MPa (0.166 × 106 psi). Additionally, the values of parametric and nonparametric Fb (design fiber stress in bending values ) were reported as 4.05 MPa and 4.54 MPa (588 psi and 659 psi), respectively. The mechanical properties of these three-ply pine mats were also compared with other studies of mats from other species groups and design architectures.
期刊介绍：
Forest Products Journal (FPJ) is the source of information for industry leaders, researchers, teachers, students, and everyone interested in today''s forest products industry.
The Forest Products Journal is well respected for publishing high-quality peer-reviewed technical research findings at the applied or practical level that reflect the current state of wood science and technology. Articles suitable as Technical Notes are brief notes (generally 1,200 words or less) that describe new or improved equipment or techniques; report on findings produced as by-products of major studies; or outline progress to date on long-term projects.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们