Computing Tire Component Durability via Critical Plane Analysis

Abstract

Tire developers are responsible for designing against the possibility of crack development in each of the various components of a tire. The task requires knowledge of the fatigue behavior of each compound in the tire, as well as adequate accounting for the multiaxial stresses carried by tire materials. The analysis is illustrated here using the Endurica CL fatigue solver for the case of a 1200R20 TBR tire operating at 837 kPa under loads ranging from 66 to 170% of rated load. The fatigue behavior of the tire's materials is described from a fracture mechanical viewpoint, with care taken to specify each of the several phenomena (crack growth rate, crack precursor size, strain crystallization, fatigue threshold) that govern. The analysis of crack development is made by considering how many cycles are required to grow cracks of various potential orientations at each element of the model. The most critical plane is then identified as the plane with the shortest fatigue life. We consider each component of the tire and show that where cracks develop from precursors intrinsic to the rubber compound (sidewall, tread grooves, innerliner) the critical plane analysis provides a comprehensive view of the failure mechanics. For cases where a crack develops near a stress singularity (i.e., belt-edge separation), the critical plane analysis remains advantageous for design guidance, particularly relative to analysis approaches based upon scalar invariant theories (i.e., strain energy density) that neglect to account for crack closure effects.