Pengaruh Penggunaan Lapisan Phase Change Material Parafin Grafit Sebagai Pendingin Terhadap Efisiensi Panel Surya Polycrystalline

Rovida Camalia Hartantrie, Ryann Argadiraksa, I Gede Eka Lesmana
{"title":"Pengaruh Penggunaan Lapisan Phase Change Material Parafin Grafit Sebagai Pendingin Terhadap Efisiensi Panel Surya Polycrystalline","authors":"Rovida Camalia Hartantrie, Ryann Argadiraksa, I Gede Eka Lesmana","doi":"10.35970/infotekmesin.v13i2.1549","DOIUrl":null,"url":null,"abstract":"Solar panels such as PLTS can be an alternative to complete electricity needs. However, the intensity and temperature of the sun that can not be adjusted are an obstacle to the use of solar panels. Continuous absorption of sunlight can cause solar panels to overheat. Therefore, it is necessary to cool the solar panels, therefore the heat absorbed does not exceed the capacity. Phase Change Material (PCM) paraffin graphite is one of the coolants for solar panels. PCM paraffin graphite was used to coat solar panels and then measured for voltage, current, and temperature. The results were compared with solar panels that were not covered with PCM paraffin graphite. The test results found that solar panels coated with PCM produced a lower surface temperature of 0.1458% than those without PCM. Meanwhile, the efficiency and power produced by PCM-coated solar panels were 19.496% and 0.02685% higher than solar panels without PCM, respectively, so the use of PCM paraffin graphite in solar panels can increase their efficiency.","PeriodicalId":33598,"journal":{"name":"Infotekmesin Media Komunikasi Ilmiah Politeknik Cilacap","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2022-07-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Infotekmesin Media Komunikasi Ilmiah Politeknik Cilacap","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.35970/infotekmesin.v13i2.1549","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0

Abstract

Solar panels such as PLTS can be an alternative to complete electricity needs. However, the intensity and temperature of the sun that can not be adjusted are an obstacle to the use of solar panels. Continuous absorption of sunlight can cause solar panels to overheat. Therefore, it is necessary to cool the solar panels, therefore the heat absorbed does not exceed the capacity. Phase Change Material (PCM) paraffin graphite is one of the coolants for solar panels. PCM paraffin graphite was used to coat solar panels and then measured for voltage, current, and temperature. The results were compared with solar panels that were not covered with PCM paraffin graphite. The test results found that solar panels coated with PCM produced a lower surface temperature of 0.1458% than those without PCM. Meanwhile, the efficiency and power produced by PCM-coated solar panels were 19.496% and 0.02685% higher than solar panels without PCM, respectively, so the use of PCM paraffin graphite in solar panels can increase their efficiency.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
相变材料石蜡图层使用管理器对多晶硅太阳能电池板效率的影响
PLTS等太阳能电池板可以作为满足电力需求的替代方案。然而,无法调节的太阳强度和温度是太阳能电池板使用的障碍。持续吸收阳光会导致太阳能板过热。因此,有必要冷却太阳能电池板,因此吸收的热量不超过容量。相变材料石蜡石墨(PCM)是太阳能电池板的冷却剂之一。用PCM石蜡石墨涂覆太阳能电池板,然后测量电压、电流和温度。结果与未覆盖PCM石蜡石墨的太阳能电池板进行了比较。测试结果发现,涂覆PCM的太阳能电池板表面温度比未涂覆PCM的太阳能电池板低0.1458%。与未涂覆PCM的太阳能电池板相比,涂覆PCM的太阳能电池板效率和发电量分别提高了19.496%和0.02685%,因此在太阳能电池板中使用PCM石蜡石墨可以提高太阳能电池板的效率。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
自引率
0.00%
发文量
30
审稿时长
12 weeks
期刊最新文献
Perhitungan Pengendalian Persediaan Fast Moving Spare Part Dengan Metode Min-Max Stock Rancang Bangun Sistem Pengisian Otomatis Merica Bubuk Berbasis Kontroler Arduino Nano Klasifikasi Opini Publik di Twitter Terhadap Bakal Calon Presiden Indonesia Tahun 2024 Menggunakan LSTM Secara Realtime Berbasis Website Optimalisasi Labview Sebagai Kendali dan Monitoring Arus Tegangan pada Modul Solar Cell Menggunakan Jaringan Lokal Analisis Kekuatan Tarik dan Regangan Filamen Carbon Fiber Hasil 3D Print dengan Variasi Fill Density
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1