{"title":"Corrosion behaviour characterisation of 316L stainless steel and Inconel 625 in supercritical water containing hydrochloric acid and high oxygen","authors":"Hongyi Zhou, Zhao Tian, Chuanhua Liao","doi":"10.1080/1478422X.2022.2112931","DOIUrl":null,"url":null,"abstract":"ABSTRACT Corrosion was currently the most crucial factor hindering the commercial development of supercritical water oxidation (SCWO) technology. Stainless steel represented by 316L and Ni-based alloy represented by Inconel 625 were performed and compared with corrosion resistance in supercritical environment with high concentrations of oxygen and chlorides. The results shown that the duplex layer was formed on two samples. The surface of 316L SS was mainly composed of loose magnetite and haematite, resulted in pitting corrosion, microcracks, and the exfoliation of oxide. The inner layer were separately a small amount of Cr2O3 oxide and FeCr2O4 spinel, which were caused by the lower content of chromium. Compared with 316L SS, the oxide film structure of Inconel 625 was composed of the outer layer of spinel and the inner layer of Cr-rich oxide. Some nodular oxides were formed, and it can be explained by the volatilisation process of chromium.","PeriodicalId":10711,"journal":{"name":"Corrosion Engineering, Science and Technology","volume":"57 1","pages":"640 - 647"},"PeriodicalIF":1.5000,"publicationDate":"2022-08-23","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Corrosion Engineering, Science and Technology","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/1478422X.2022.2112931","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 3
Abstract
ABSTRACT Corrosion was currently the most crucial factor hindering the commercial development of supercritical water oxidation (SCWO) technology. Stainless steel represented by 316L and Ni-based alloy represented by Inconel 625 were performed and compared with corrosion resistance in supercritical environment with high concentrations of oxygen and chlorides. The results shown that the duplex layer was formed on two samples. The surface of 316L SS was mainly composed of loose magnetite and haematite, resulted in pitting corrosion, microcracks, and the exfoliation of oxide. The inner layer were separately a small amount of Cr2O3 oxide and FeCr2O4 spinel, which were caused by the lower content of chromium. Compared with 316L SS, the oxide film structure of Inconel 625 was composed of the outer layer of spinel and the inner layer of Cr-rich oxide. Some nodular oxides were formed, and it can be explained by the volatilisation process of chromium.
期刊介绍：
Corrosion Engineering, Science and Technology provides broad international coverage of research and practice in corrosion processes and corrosion control. Peer-reviewed contributions address all aspects of corrosion engineering and corrosion science; there is strong emphasis on effective design and materials selection to combat corrosion and the journal carries failure case studies to further knowledge in these areas.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们