The effect of Pd and Ni coatings on hydrogen permeation experiments of as-quenched martensitic steel

IF 2.7 4区 材料科学 Q3 ELECTROCHEMISTRY Corrosion Reviews Pub Date : 2023-05-15 DOI:10.1515/corrrev-2022-0118
R. Latypova, T. Nyo, O. Seppälä, Kasper Hahtonen, H. Hänninen, J. Kömi, S. Pallaspuro
{"title":"The effect of Pd and Ni coatings on hydrogen permeation experiments of as-quenched martensitic steel","authors":"R. Latypova, T. Nyo, O. Seppälä, Kasper Hahtonen, H. Hänninen, J. Kömi, S. Pallaspuro","doi":"10.1515/corrrev-2022-0118","DOIUrl":null,"url":null,"abstract":"Abstract Hydrogen permeation technique is a widely used testing method for the determination of hydrogen diffusion coefficient (D), which is an important parameter considering hydrogen embrittlement. A palladium (Pd) or nickel (Ni) coating is often utilised on the hydrogen detection side of the test specimens. Here, we investigate the effect of Pd and Ni coatings on hydrogen diffusion in a martensitic 500 HBW hardness low-alloy steel in the thickness range of 0.5 – 0.8 mm using a refined successive transient method and compare against an uncoated reference specimen. Both coatings yield similar average D values (6 – 6.6 × 10−7 cm2/s), but the best repeatability is achieved with Pd coating. With Ni coating, D values decrease with the increasing specimen thickness, which is partly caused by a slower hydrogen diffusion in Ni, and therefore a concentration gradient at the specimen-coating interface. The uncoated specimen has a poor transient fit, and significantly lower D (2.1 × 10−7 cm2/s) due to surface oxidation. With both coatings, the steepness of the last decay transient was highly affected by specimen thickness, and therefore the density of reversible hydrogen traps is only comparable for similar thicknesses.","PeriodicalId":10721,"journal":{"name":"Corrosion Reviews","volume":null,"pages":null},"PeriodicalIF":2.7000,"publicationDate":"2023-05-15","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Corrosion Reviews","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1515/corrrev-2022-0118","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"ELECTROCHEMISTRY","Score":null,"Total":0}
引用次数: 1

Abstract

Abstract Hydrogen permeation technique is a widely used testing method for the determination of hydrogen diffusion coefficient (D), which is an important parameter considering hydrogen embrittlement. A palladium (Pd) or nickel (Ni) coating is often utilised on the hydrogen detection side of the test specimens. Here, we investigate the effect of Pd and Ni coatings on hydrogen diffusion in a martensitic 500 HBW hardness low-alloy steel in the thickness range of 0.5 – 0.8 mm using a refined successive transient method and compare against an uncoated reference specimen. Both coatings yield similar average D values (6 – 6.6 × 10−7 cm2/s), but the best repeatability is achieved with Pd coating. With Ni coating, D values decrease with the increasing specimen thickness, which is partly caused by a slower hydrogen diffusion in Ni, and therefore a concentration gradient at the specimen-coating interface. The uncoated specimen has a poor transient fit, and significantly lower D (2.1 × 10−7 cm2/s) due to surface oxidation. With both coatings, the steepness of the last decay transient was highly affected by specimen thickness, and therefore the density of reversible hydrogen traps is only comparable for similar thicknesses.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Pd和Ni涂层对淬火马氏体钢渗氢实验的影响
摘要氢渗透技术是测定氢扩散系数(D)的一种广泛使用的测试方法,氢扩散系数是考虑氢脆的一个重要参数。钯(Pd)或镍(Ni)涂层通常用于试样的氢检测侧。在这里,我们研究了Pd和Ni涂层对马氏体500中氢扩散的影响 HBW硬度低合金钢,厚度范围为0.5–0.8 mm,并与未涂覆的参考样品进行比较。两种涂层的平均D值相似(6–6.6×10−7 cm2/s),但是用Pd涂层实现了最佳的可重复性。对于Ni涂层,D值随着试样厚度的增加而减小,这在一定程度上是由Ni中较慢的氢扩散引起的,因此是由试样-涂层界面处的浓度梯度引起的。未涂覆试样的瞬态拟合较差,且D明显较低(2.1×10−7 cm2/s)。对于这两种涂层,最后一次衰变瞬态的陡度在很大程度上受到样品厚度的影响,因此可逆氢陷阱的密度仅在类似厚度下可比较。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Corrosion Reviews
Corrosion Reviews 工程技术-材料科学:膜
CiteScore
5.20
自引率
3.10%
发文量
44
审稿时长
4.5 months
期刊介绍: Corrosion Reviews is an international bimonthly journal devoted to critical reviews and, to a lesser extent, outstanding original articles that are key to advancing the understanding and application of corrosion science and engineering in the service of society. Papers may be of a theoretical, experimental or practical nature, provided that they make a significant contribution to knowledge in the field.
期刊最新文献
Investigation of corrosion inhibition and adsorption properties of quinoxaline derivatives on metal surfaces through DFT and Monte Carlo simulations Phytochemicals as eco-friendly corrosion inhibitors for mild steel in sulfuric acid solutions: a review Corrosion mechanism of K411 superalloy in sulfur-containing environment: sulfidation promoting internal nitridation The impact of loading rate on chloride induced stress corrosion cracking of 304L stainless steel On relating quasi-static load threshold K1scc to K1c
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1