Moisture is not always bad: H2O accelerates the conversion of DMAPbI3 intermediate to CsPbI3 for boosting the efficiency of carbon-based perovskite solar cells to over 16%

Abstract

Inorganic CsPbI₃ perovskite has exhibited great application potential in perovskite solar cells (PSCs) due to its suitable optical bandgap and high chemical stability. However, the perovskite phases of CsPbI₃ are not stable at room temperature, where they transition to non-perovskite phases. Humidity or water has been thought to be the primary factor inducing this phase transition, which should be avoided throughout the procedure of film and device processing. Surprisingly, the present study indicates that preparing a precursor solution in humid air is beneficial to the growth of high-quality CsPbI₃ perovskite to enhance device performance. It is demonstrated that the incorporation of H₂O in the precursor solution from humid air or by intentional addition significantly changes the composition of coordination compounds and increases the amount of low iodine coordination complexes. As a result, the crystallization of dimethylammonium lead iodide (DMAPbI₃) intermediate is suppressed well, which accelerates its subsequent conversion to CsPbI₃ perovskite. Consequently, an oriented CsPbI₃ perovskite film with improved crystallinity and lower defect density is obtained. Most importantly, carbon-based PSCs (C-PSCs) based on the CsPbI₃ perovskite film achieve an efficiency of 16.05%, a new record for inorganic C-PSCs.