Study of the Effect of Modification of Asphalt on the Rheological Properties Employing Microwave Radiation—An Aging Study

Abstract

This study focuses on producing asphalt with improved rheological properties that differ from the original asphalt and are less affected by aging conditions. The rheological properties of Qayara asphalt were enhanced by modifying the asphalt using spent rubber tire (SRT) with different percentages of anhydrous aluminum chloride. Percentages ranging from 1.0% by weight of the spent tire rubber were added after proceeding with the thermal crushing process. The percentages of anhydrous aluminum chloride catalyst were 0.4 and 0.8%, respectively. This mixture was microwaved at 270 watt of power for 4, 8, and 12 min, respectively. The measurements performed are plasticity, penetration, softening point, and penetration index. The previously mentioned measurements were also made on the modified asphalt one year after the modification process to understand the effect of aging conditions. The microstructure and thermodynamics have been characterized by FE-SEM and EDX measurements. This study provides good rheological properties of the modified bitumen binder that is aging-resistant.