Renan Belli , Susanne S. Scherrer , Ulrich Lohbauer
{"title":"Report on fractures of trilayered all-ceramic fixed dental prostheses","authors":"Renan Belli , Susanne S. Scherrer , Ulrich Lohbauer","doi":"10.1016/j.csefa.2016.10.001","DOIUrl":null,"url":null,"abstract":"<div><p>Three cases of trilayered fixed dental prostheses fractured in vivo are fractographically analyzed to identify causes of failure. In all cases fractures initiated from a preexistent crack/defect in the zirconia framework produced previous to the fusion firing of a lithium disilicate veneering ceramic. In two cases zirconia framework pre-cracks were found to have been infiltrated with the intermediate fusion glass that diffused therein during sintering. This report highlights the susceptibility of zirconia to grinding damage and its role in limiting the lifetime of zirconia-based fixed dental prostheses.</p></div>","PeriodicalId":91224,"journal":{"name":"Case studies in engineering failure analysis","volume":"7 ","pages":"Pages 71-79"},"PeriodicalIF":0.0000,"publicationDate":"2016-10-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1016/j.csefa.2016.10.001","citationCount":"20","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Case studies in engineering failure analysis","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S221329021630027X","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 20
Abstract
Three cases of trilayered fixed dental prostheses fractured in vivo are fractographically analyzed to identify causes of failure. In all cases fractures initiated from a preexistent crack/defect in the zirconia framework produced previous to the fusion firing of a lithium disilicate veneering ceramic. In two cases zirconia framework pre-cracks were found to have been infiltrated with the intermediate fusion glass that diffused therein during sintering. This report highlights the susceptibility of zirconia to grinding damage and its role in limiting the lifetime of zirconia-based fixed dental prostheses.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们