Bacteriological and Mechanical Evaluation of Antibacterial Filler-Containing Composite Resins

Teuku Syafiuddin, T. Igarashi, H. Shimomura, H. Hisamitsu, N. Goto
{"title":"Bacteriological and Mechanical Evaluation of Antibacterial Filler-Containing Composite Resins","authors":"Teuku Syafiuddin, T. Igarashi, H. Shimomura, H. Hisamitsu, N. Goto","doi":"10.11516/DENTALMEDRES1981.13.443","DOIUrl":null,"url":null,"abstract":"The antibacterial effect restorative materials is important for obtaining good prognosis. The purpose of this study was to evaluate the antibacterial effect of trial composite resins which were made with Clearfil SC II and antibacterial powder as a filler. Four kinds of antibacterial powder were used: two kinds of Cellewall; far infrared radiating ceramic materials YYT 1 and YYT 1A, Bactekiller; antibacterial zeolite and Zeomic; zeolite with antibacterial ion were mixed with Clearfil SC II at the content of 5, 10, 15, 20, 30, 40, 50 wt %. Cariogenic bacteria Streptococcus mutans Ingbritt, was used in this experiment. Disks were placed in petri dishes and the width of inhibitory zone was evaluated after 24 hours. In order to evaluate the effect of saline solution, the disks were stored in saline solution for 24 and 48 hours and the inhibitory zone were also evaluated same condition. The conclusion is that the new composite resins containing Zeomic had a strong antibacterial effect against S. mutans and this effect of Zeomic was not reduced after storage in saline solution.","PeriodicalId":77624,"journal":{"name":"Showa Shigakkai zasshi = The Journal of Showa University Dental Society","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"1993-12-31","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"7","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Showa Shigakkai zasshi = The Journal of Showa University Dental Society","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.11516/DENTALMEDRES1981.13.443","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 7

Abstract

The antibacterial effect restorative materials is important for obtaining good prognosis. The purpose of this study was to evaluate the antibacterial effect of trial composite resins which were made with Clearfil SC II and antibacterial powder as a filler. Four kinds of antibacterial powder were used: two kinds of Cellewall; far infrared radiating ceramic materials YYT 1 and YYT 1A, Bactekiller; antibacterial zeolite and Zeomic; zeolite with antibacterial ion were mixed with Clearfil SC II at the content of 5, 10, 15, 20, 30, 40, 50 wt %. Cariogenic bacteria Streptococcus mutans Ingbritt, was used in this experiment. Disks were placed in petri dishes and the width of inhibitory zone was evaluated after 24 hours. In order to evaluate the effect of saline solution, the disks were stored in saline solution for 24 and 48 hours and the inhibitory zone were also evaluated same condition. The conclusion is that the new composite resins containing Zeomic had a strong antibacterial effect against S. mutans and this effect of Zeomic was not reduced after storage in saline solution.
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
含抗菌填料复合树脂的细菌学和力学评价
修复材料的抗菌效果是获得良好预后的重要因素。本研究的目的是评价以Clearfil SC II和抗菌粉为填料制备的复合树脂的抗菌效果。采用四种抗菌粉剂:两种celllewall;远红外辐射陶瓷材料yyt1和YYT 1A,抗菌剂;抗菌沸石和Zeomic;含抗菌离子的沸石与Clearfil SC II分别以5、10、15、20、30、40、50 wt %的比例混合。本实验采用致龋菌英氏变形链球菌。将培养皿置于培养皿中,24小时后评估抑菌带宽度。为了评估生理盐水的效果,将培养皿在生理盐水中保存24和48小时,并在相同的条件下评估抑菌带。综上所述,Zeomic复合树脂对变形链球菌具有较强的抑菌作用,且Zeomic在生理盐水中保存后其抑菌作用不降低。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
自引率
0.00%
发文量
0
期刊最新文献
術前顎矯正治療(NAM)が哺乳へ与える影響について 裂型別にみる哺乳障害の現状アンケート調査 SEM and TEM Observation of Ultra Microstructure at Adhesive Interface between Resin and Caries Affected Dentin Suppression of Visceromotor Function Induced by Noxious Stimulation to the Oral-facial Region in the Rat Noggin Prevents Osteogenesis but Induces Chondrogenesis in a Human Mesenchymal Cell Line (USAC) Electromyographic Evaluation of Masticatory Muscles Following Surgical Orthodontics with Skeletal Mandibular Prognathism
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1