{"title":"Oxidation and hot corrosion behavior of a directionally solidified W richen cobalt-based superalloy","authors":"Yue Zhou, C. Mo, Hong Wang","doi":"10.1051/METAL/2021033","DOIUrl":null,"url":null,"abstract":"In this study, isothermal and hot corrosion in molten 75 mass% Na2 SO4 +25 mass% NaCl at 900 °C was carried out on an W richen Co-based directionally solidified Co-27.53Cr-9.85W-10.29Ni-0.75Al superalloy. For comparison, K38G with composition of 16.34Cr-4Al-1.77Mo-3.81Ti-2.66W-8.38Co were also conducted under same condition. Isothermal oxidation indicates that Co-based superalloy forms a Co-oxide dispersion chromia scale. However, K38G forms a purer chromia scale due to higher weight percentage ratio of Cr to Al. Under molten Na2 SO4 -NaCl salts, the defects in Ni/Co oxide dispersion chromia layer make it feasible that the molten salt can penetrates along grain boundaries into the internal interface to form internal sulfides, which causes the spallation of scales and significantly decreases its hot corrosion resistance.","PeriodicalId":18527,"journal":{"name":"Metallurgical Research & Technology","volume":"13 1","pages":"313"},"PeriodicalIF":0.9000,"publicationDate":"2021-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Metallurgical Research & Technology","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1051/METAL/2021033","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 0
Abstract
In this study, isothermal and hot corrosion in molten 75 mass% Na2 SO4 +25 mass% NaCl at 900 °C was carried out on an W richen Co-based directionally solidified Co-27.53Cr-9.85W-10.29Ni-0.75Al superalloy. For comparison, K38G with composition of 16.34Cr-4Al-1.77Mo-3.81Ti-2.66W-8.38Co were also conducted under same condition. Isothermal oxidation indicates that Co-based superalloy forms a Co-oxide dispersion chromia scale. However, K38G forms a purer chromia scale due to higher weight percentage ratio of Cr to Al. Under molten Na2 SO4 -NaCl salts, the defects in Ni/Co oxide dispersion chromia layer make it feasible that the molten salt can penetrates along grain boundaries into the internal interface to form internal sulfides, which causes the spallation of scales and significantly decreases its hot corrosion resistance.
期刊介绍：
Metallurgical Research and Technology (MRT) is a peer-reviewed bi-monthly journal publishing original high-quality research papers in areas ranging from process metallurgy to metal product properties and applications of ferrous and non-ferrous metals and alloys, including light-metals. It covers also the materials involved in the metal processing as ores, refractories and slags.
The journal is listed in the citation index Web of Science and has an Impact Factor.
It is highly concerned by the technological innovation as a support of the metallurgical industry at a time when it has to tackle severe challenges like energy, raw materials, sustainability, environment... Strengthening and enhancing the dialogue between science and industry is at the heart of the scope of MRT. This is why it welcomes manuscripts focusing on industrial practice, as well as basic metallurgical knowledge or review articles.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们