Behaviour of a silica filler surface‐modified with boron‐amine groups

Abstract

The behaviour of silica fillers modified with primary boron-amine groups has been studied under different reaction conditions. The filler with the best reinforcing properties was used to compare two different vulcanization systems: an efficient vulcanization system, EV, which is the recommended ISO Standards method to study the reinforcing behaviour of new silicas, and a conventional vulcanization system. The results indicate that the best properties are obtained with silica treated for 3 h at 500°C, reaction conditions which fix most of the primary boron-amine groups. Using the EV system, the properties of this modified silica are similar to those of silane-modified silica, and in some cases better than those obtained with a conventional vulcanization system. In all cases, the boron-amination treatment significantly improves the behaviour of precipitated silica as a reinforcing filler. Das Verhalten von mit primaren Boramingruppen modifizierten Silikat-Fullstoffen wurde unter verschiedenen Reaktionsbedingungen untersucht. Der Fullstoff mit den besten Verstarkungseigenschaften wurde eingesetzt, um zwei unterschiedliche Vulkanisationssysteme zu vergleichen: ein wirksames Vulkanisationsverfahren (EV), das nach ISO als Methode zur Untersuchung des Verstarkungsverhaltens neuer Silikate empfohlen wird, sowie ein konventionelles Verfahren. Die besten Ergebnisse werden mit Silikat erhalten, welches 3 h bei 500°C behandelt wurde; unter diesen Bedingungen werden die meisten der primaren Boramingruppen fixiert. Die Eigenschaften des nach dem EV-Verfahren modifizierten Silikats ahneln denen von mit Silan modifizierten Silikaten und sind in einigen Fallen besser als jene, welche nach dem konventionellen Verfahren erhalten werden. In allen Fallen wird die verstarkende Wirkung von gefallten Silikat-Fullstoffen durch die Boraminbehandlung verbessert.