{"title":"Microstructural Characterization and Corrosion Behavior of Electroless Ni-Zn-P Thin Films","authors":"I. Constantin","doi":"10.1155/2014/827393","DOIUrl":null,"url":null,"abstract":"Ternary Ni-Zn-P alloy thin films were electrolessly deposited on a carbon steel substrate from sulphate alkaline baths. The effect of deposition bath composition and process duration on the physical-chemical and corrosion characteristics of the obtained thin films was investigated. The thin films were characterized by EDAX analysis techniques and scanning electronic microscopy. Corrosion tests were performed in 3.5% sodium chloride solution and the corrosion current values were determined to be 4–12 μA, comparative to 15 μA for the uncoated steel sample.","PeriodicalId":16342,"journal":{"name":"Journal of Metallurgy","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2014-01-27","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"13","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Metallurgy","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1155/2014/827393","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 13
Abstract
Ternary Ni-Zn-P alloy thin films were electrolessly deposited on a carbon steel substrate from sulphate alkaline baths. The effect of deposition bath composition and process duration on the physical-chemical and corrosion characteristics of the obtained thin films was investigated. The thin films were characterized by EDAX analysis techniques and scanning electronic microscopy. Corrosion tests were performed in 3.5% sodium chloride solution and the corrosion current values were determined to be 4–12 μA, comparative to 15 μA for the uncoated steel sample.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们