{"title":"Characteristic and Identification of Bleached and Filled Aquamarine","authors":"Jia Qiong, LI Guogui, Li Xueming, X. Yao, Wang Hailong, Luo Junqi","doi":"10.15964/J.CNKI.027JGG.2021.05.005","DOIUrl":null,"url":null,"abstract":"The aquamarine samples were collected from gem factories and jewelry markets, and the gemmological characteristics, infrared spectra and fluorescence images were tested and analyzed. The results showed that blue flashes and bubles can be seen in the sample when magnified. Infrared spectra showed a group of absorption peaks related to epoxy resin near 2 879, 2 932, 2 962, 3 035 cm-1 and 3 055 cm-1indicating that the samples have been filled. Through magnification, cracks can be seen on the surface of the samples. The fluorescence images under DiamondViewTM showed that bluish white fluorescence interlaces densely in the sample. The micro-infrared spectra showed the absorption peaks related to epoxy resin in the central area of sample slices, indicating that the sample structure was damaged and the filling degree was serious. Such samples should be named \"bleached and filled aquamarine\" according to the China national standard Gems-Nomenclature.","PeriodicalId":15852,"journal":{"name":"Journal of Gems & Gemmology","volume":"199 1","pages":"43-50"},"PeriodicalIF":0.0000,"publicationDate":"2021-09-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Gems & Gemmology","FirstCategoryId":"1089","ListUrlMain":"https://doi.org/10.15964/J.CNKI.027JGG.2021.05.005","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0
Abstract
The aquamarine samples were collected from gem factories and jewelry markets, and the gemmological characteristics, infrared spectra and fluorescence images were tested and analyzed. The results showed that blue flashes and bubles can be seen in the sample when magnified. Infrared spectra showed a group of absorption peaks related to epoxy resin near 2 879, 2 932, 2 962, 3 035 cm-1 and 3 055 cm-1indicating that the samples have been filled. Through magnification, cracks can be seen on the surface of the samples. The fluorescence images under DiamondViewTM showed that bluish white fluorescence interlaces densely in the sample. The micro-infrared spectra showed the absorption peaks related to epoxy resin in the central area of sample slices, indicating that the sample structure was damaged and the filling degree was serious. Such samples should be named "bleached and filled aquamarine" according to the China national standard Gems-Nomenclature.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们