Antistatic modification of polyester with carboxyterminated poly(oxyethylene)

Abstract

Carboxy-terminated poly(oxyethylenes) (PEO-acid) with number-average molecular weights Mn = 8400, 3300, and 1000 were used for antielectrostatic modification of poly(ethylene terephthalate) (PET). The blend PET fibers containing 2.0 and 5.0 wt.-% of PEO-acids were melt-spun at 285°C with an ordinary extruder and then drawn about 4.5-fold at 80°C. The processabilities of spinning and drawing were excellent at higher molecular weights of PEO-acid. The anti-electrostatic properties of the blend fibers became also improved with increasing molecular weight of PEO-acid. Since little ester interchange reaction took place between PET and PEO-acid during meltspinning, the blend fibers could retain almost the same mechanical properties as the original PET fiber. Carboxy-terminierte Polyoxyethylene (PEO-acid) mit zahlenmittleren Molekulargewichten Mn = 8400, 3300 und 1000 wurden zur antielektrostatischen Modifizierung von Polyethylenterephthalat (PET) verwendet. Fasern aus PET-PEO-acid-Blends mit 2,0 oder 5,0 Gew.-% PEO-acid wurden bei 285°C mit einem normalen Extruder aus der Schmelze gesponnen und anschliesend bei 80°C um das ca. 4,5fache verstreckt. Die Verarbeitbarkeit beim Verspinnen und Verstrecken war bei Verwendung von PEO-acid mit hohen Molekulargewichten ausgezeichnet. Die anti-elektrostatischen Eigenschaften wurden ebenfalls mit steigendem PEO-acid-Molekulargewicht besser. Da eine Umesterung beim Verspinnen nur in geringem Ausmas stattfand, blieben die mechanischen Eigenschaften der Blend-Fasern gegenuber den PET-Fasern nahezu unverandert.