J. Alias, N. S. Mohamed, M. Ishak, Xiorong Zhou, G. Thompson
{"title":"The Influence of Hot Forming on the Microstructure and Corrosion Behaviour of AZ31B Magnesium Alloys","authors":"J. Alias, N. S. Mohamed, M. Ishak, Xiorong Zhou, G. Thompson","doi":"10.17509/IJOST.V3I2.12758","DOIUrl":null,"url":null,"abstract":"The influence of the hot forming process of AZ31B wrought and twin roll cast (TRC) magnesium alloy sheets on the microstructure and corrosion behaviour have been evaluated. The corrosion behaviour was investigated by hydrogen evolution experiments in chloride-containing solution. Filiform-like corrosion was predominant attack to the AZ31 magnesium alloys, as observed by in-situ corrosion observation. The intermetallic particle existence and grain structure significantly influenced the corrosion rate. The dendritic structure of the as-cast TRC alloy was severely attacked, revealing that the as-cast alloy was highly susceptible to corrosion. The presence of twins in wrought alloy was found to act as a corrosion barrier, while the increase in grain size showed the high corrosion rate of the alloy.","PeriodicalId":37185,"journal":{"name":"Indonesian Journal of Science and Technology","volume":"1 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2018-08-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Indonesian Journal of Science and Technology","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.17509/IJOST.V3I2.12758","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"Earth and Planetary Sciences","Score":null,"Total":0}
引用次数: 0
Abstract
The influence of the hot forming process of AZ31B wrought and twin roll cast (TRC) magnesium alloy sheets on the microstructure and corrosion behaviour have been evaluated. The corrosion behaviour was investigated by hydrogen evolution experiments in chloride-containing solution. Filiform-like corrosion was predominant attack to the AZ31 magnesium alloys, as observed by in-situ corrosion observation. The intermetallic particle existence and grain structure significantly influenced the corrosion rate. The dendritic structure of the as-cast TRC alloy was severely attacked, revealing that the as-cast alloy was highly susceptible to corrosion. The presence of twins in wrought alloy was found to act as a corrosion barrier, while the increase in grain size showed the high corrosion rate of the alloy.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们