{"title":"Synthesis and Properties of a Flexible Curing Agent","authors":"X. Wang","doi":"10.14233/ajchem.2013.13936","DOIUrl":null,"url":null,"abstract":"This paper presents the synthesis of a new type of flexible epoxy curing agent and an approach to improve the toughness of epoxy resin by curing without reducing the strength and modulus of the resin-cured material.The results show that the degree of toughness reaches maximum values when the flexible curing agent is applied at weight percentages( wt. %) between 10% and 15%. When the amount of flexible curing agent added to epoxy resin weight is 10 wt. %,the impact toughness and fracture toughness increases by 33. 3% and 96. 3%,respectively,compared with the pure epoxy resin. When the amount of flexible curing agent added to epoxy is 10 wt. %,the resulting impact toughness of the material is 19. 5k J·m-2at-50℃,the impact toughness of pure epoxy resin is only7. 96 k J·m-2.","PeriodicalId":22171,"journal":{"name":"合成材料老化与应用","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2015-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"合成材料老化与应用","FirstCategoryId":"1087","ListUrlMain":"https://doi.org/10.14233/ajchem.2013.13936","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 1
Abstract
This paper presents the synthesis of a new type of flexible epoxy curing agent and an approach to improve the toughness of epoxy resin by curing without reducing the strength and modulus of the resin-cured material.The results show that the degree of toughness reaches maximum values when the flexible curing agent is applied at weight percentages( wt. %) between 10% and 15%. When the amount of flexible curing agent added to epoxy resin weight is 10 wt. %,the impact toughness and fracture toughness increases by 33. 3% and 96. 3%,respectively,compared with the pure epoxy resin. When the amount of flexible curing agent added to epoxy is 10 wt. %,the resulting impact toughness of the material is 19. 5k J·m-2at-50℃,the impact toughness of pure epoxy resin is only7. 96 k J·m-2.