{"title":"Preparation and oxidation behaviour of MoSi2-SiC-Si-ZrB2 composite coatings on carbon surface via laser cladding","authors":"Xuemei Liu, Weixin Chen, X. Tao, Heliang Fan, Zhangsheng Liu, Y. Ling, Litong Guo","doi":"10.1080/17436753.2022.2155372","DOIUrl":null,"url":null,"abstract":"ABSTRACT Anti-oxidation coatings of MoSi2-SiC-Si-ZrB2 were prepared on the graphite surface by laser cladding. The XRD, scratching bonding force, SEM and isothermal oxidation tests were used to investigate the microstructure and properties of the coatings. The coating with 40 wt% ZrB2 added (MoSi2:SiC:Si:ZrB2 = 16:4:5:16.6) has the lowest degree of oxidation, the best oxidation resistance and the highest bonding strength between coating and matrix. The scratching bonding force still maintained at about 9.9 N after laser ablation, and there were no obvious destructive defects but some pores and cracks on the coating. After a Si-enriched amorphous layer was formed, the relative oxygen permeability was significantly decreased and the oxidation of the coating was passivated, which prevented the matrix from further oxidation.","PeriodicalId":7224,"journal":{"name":"Advances in Applied Ceramics","volume":"1 1","pages":"202 - 210"},"PeriodicalIF":1.3000,"publicationDate":"2022-11-17","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Advances in Applied Ceramics","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/17436753.2022.2155372","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, CERAMICS","Score":null,"Total":0}
引用次数: 0
Abstract
ABSTRACT Anti-oxidation coatings of MoSi2-SiC-Si-ZrB2 were prepared on the graphite surface by laser cladding. The XRD, scratching bonding force, SEM and isothermal oxidation tests were used to investigate the microstructure and properties of the coatings. The coating with 40 wt% ZrB2 added (MoSi2:SiC:Si:ZrB2 = 16:4:5:16.6) has the lowest degree of oxidation, the best oxidation resistance and the highest bonding strength between coating and matrix. The scratching bonding force still maintained at about 9.9 N after laser ablation, and there were no obvious destructive defects but some pores and cracks on the coating. After a Si-enriched amorphous layer was formed, the relative oxygen permeability was significantly decreased and the oxidation of the coating was passivated, which prevented the matrix from further oxidation.
期刊介绍：
Advances in Applied Ceramics: Structural, Functional and Bioceramics provides international coverage of high-quality research on functional ceramics, engineering ceramics and bioceramics.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们