C. L. Xu, T. Andriollo, Yubin Zhang, J. C. Hernando, J. Hattel, N. Tiedje
{"title":"Micromechanical Impact of Solidification Regions in Ductile Iron Revealed Via a 3D Strain Partitioning Analysis Method","authors":"C. L. Xu, T. Andriollo, Yubin Zhang, J. C. Hernando, J. Hattel, N. Tiedje","doi":"10.2139/ssrn.3485109","DOIUrl":null,"url":null,"abstract":"Abstract Strain partitioning between first-to-solidify (FTS) and last-to-solidify (LTS) regions upon tensile loading of ductile iron was investigated by combining in-situ X-ray tomography with digital volume correlation and postmortem metallographic examinations. The results indicate that the plastic shear bands form mainly by linking graphite particles contained in the same FTS region. A special distance function is introduced to show that this is due to the lower strength of the FTS regions compared to the LTS regions, but also to the higher stress concentration associated with the particles. The methodology is general and therefore extendable to material systems containing similar microstructural heterogeneities.","PeriodicalId":7765,"journal":{"name":"AMI: Scripta Materialia","volume":"6 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2020-03-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"11","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"AMI: Scripta Materialia","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2139/ssrn.3485109","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 11
Abstract
Abstract Strain partitioning between first-to-solidify (FTS) and last-to-solidify (LTS) regions upon tensile loading of ductile iron was investigated by combining in-situ X-ray tomography with digital volume correlation and postmortem metallographic examinations. The results indicate that the plastic shear bands form mainly by linking graphite particles contained in the same FTS region. A special distance function is introduced to show that this is due to the lower strength of the FTS regions compared to the LTS regions, but also to the higher stress concentration associated with the particles. The methodology is general and therefore extendable to material systems containing similar microstructural heterogeneities.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们