Undercooling for Nucleation and Volume Fraction of Primary β -Sn Phase in Sn-X Alloys

IF 0.5 4区 材料科学 Q4 METALLURGY & METALLURGICAL ENGINEERING Journal of The Japan Institute of Metals Pub Date : 2017-01-01 DOI:10.2320/JINSTMET.J2016041
R. Yoshimura, S. Nagaoka, Yasuhiro Nagatomo, H. Esaka, K. Shinozuka
{"title":"Undercooling for Nucleation and Volume Fraction of Primary β -Sn Phase in Sn-X Alloys","authors":"R. Yoshimura, S. Nagaoka, Yasuhiro Nagatomo, H. Esaka, K. Shinozuka","doi":"10.2320/JINSTMET.J2016041","DOIUrl":null,"url":null,"abstract":"The undercooling for nucleation and volume fraction of primary (β–Sn) phase has been investigated in Sn–X hypoeutectic alloys where X were Pb, Ag, Al, Bi, Cu and Zn. The purities of raw materials were 4N and the solute content of the alloy was set for the volume fraction of primary phase to be from 0.3 to 0.45, according to the equilibrium phase diagram. Thermal history was measured during solidification of 5 g alloy sample at a cooling rate of 0.05 K/s, with fine K–type thermocouple. The volume fraction of primary (β–Sn) phase was measured on the longitudinal cross section of the sample. When the solute elements were Pb, Ag, Al, Bi and Cu, the undercooling was more than 5K and was large. Furthermore, the volume fraction of primary (β–Sn) was larger than the equilibrium value. On the other hand, when the solute element was Zn, the undercooling for the nucleation of primary (β–Sn) was 0.9 K and quite small. In addition to this, the volume fraction of primary phase agreed with the equilibrium value. [doi:10.2320/jinstmet.J2016041]","PeriodicalId":17337,"journal":{"name":"Journal of The Japan Institute of Metals","volume":"40 1","pages":"80-88"},"PeriodicalIF":0.5000,"publicationDate":"2017-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"3","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of The Japan Institute of Metals","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.2320/JINSTMET.J2016041","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
引用次数: 3

Abstract

The undercooling for nucleation and volume fraction of primary (β–Sn) phase has been investigated in Sn–X hypoeutectic alloys where X were Pb, Ag, Al, Bi, Cu and Zn. The purities of raw materials were 4N and the solute content of the alloy was set for the volume fraction of primary phase to be from 0.3 to 0.45, according to the equilibrium phase diagram. Thermal history was measured during solidification of 5 g alloy sample at a cooling rate of 0.05 K/s, with fine K–type thermocouple. The volume fraction of primary (β–Sn) phase was measured on the longitudinal cross section of the sample. When the solute elements were Pb, Ag, Al, Bi and Cu, the undercooling was more than 5K and was large. Furthermore, the volume fraction of primary (β–Sn) was larger than the equilibrium value. On the other hand, when the solute element was Zn, the undercooling for the nucleation of primary (β–Sn) was 0.9 K and quite small. In addition to this, the volume fraction of primary phase agreed with the equilibrium value. [doi:10.2320/jinstmet.J2016041]
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
过冷对Sn-X合金初生β -Sn相形核和体积分数的影响
研究了含Pb、Ag、Al、Bi、Cu和Zn的Sn-X亚共晶合金的过冷形核和初生(β-Sn)相的体积分数。原料纯度为4N,根据平衡相图,将合金溶质含量设定为初相体积分数为0.3 ~ 0.45。在0.05 K/s的冷却速率下,用K型热电偶测量了5 g合金试样的凝固热历史。在样品的纵截面上测量了初生相(β-Sn)的体积分数。当溶质元素为Pb、Ag、Al、Bi和Cu时,过冷度大于5K,过冷度较大。而且,初生产物(β-Sn)的体积分数大于平衡值。另一方面,当溶质元素为Zn时,初生晶(β-Sn)的过冷度为0.9 K,且过冷度很小。此外,初级相的体积分数与平衡值一致。(doi: 10.2320 / jinstmet.J2016041)
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 去求助
来源期刊
Journal of The Japan Institute of Metals
Journal of The Japan Institute of Metals 工程技术-冶金工程
CiteScore
0.70
自引率
0.00%
发文量
27
审稿时长
6-12 weeks
期刊介绍: Information not localized
期刊最新文献
The Effect of Rhodium Addition on Degradation Behavior of Ir-10 mass%Rh Alloy during Oxidation at Elevated Temperatures Changes in Carburized Microstructures and Creep Properties of Nb-Added SCH13A Heat-Resistant Cast Steel due to Different Pouring Temperatures 高温プレスを利用した加工熱処理によるMg-9Al-1Zn-2Ca合金板の機械的特性向上 Ni基単結晶超合金TMS-238のデンドライト偏析とクリープ強度におよぼす溶体化熱処理の影響 Hydrogen and Materials Characteristic in Solids V
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1