FORMING AN EDGED CUBIC TEXTURE IN BAND SUBSTRATES MADE OF (Cu+Ni)–Me (Me=Mo, Mn, Nb) ALLOYS FOR HIGH-TEMPERATURE SECOND-GENERATION SUPERCONDUCTORS

After cold-rolling reduction with the shrinkage of more than 97 % and recrystallization annealing, the edged cubic texture develops in some fcc lattice metals with the high and medium values of stacking fault energy such as Ni, Cu, Al, Pt, and some alloys on their base. The extended bands of metals and fcc lattice alloys can be used to apply multilayer functional compositions. The authors studied the structure and crystallographic texture in bands of three-component copper-nickel-based alloys. The study showed the crucial possibility of creating multi-component alloys based on the Cu+40% Ni binary alloy doped with such elements as Mo or Nb. The paper considers the formation of an edged cubic texture in bands of Cu–Ni–Mn, Cu–Ni–Nb, and Cu–Ni–Мо alloys produced through cold deformation with rolling and recrystallization annealing performed at different temperatures. The study identified that annealing during one hour at 1050 °С was an optimal recrystallization annealing mode when on the surface of bands made of (Cu+40 % Ni)–Me alloys (where Me=Mn, Mo, Nb) deformed at ~99 %, the most perfect cubic texture was realized. According to the data obtained, after such annealing mode, from 94% to 98% of grains with orientation {001}<100> developed in the Cu–40% Ni–1.3% Mn, Cu–40% Ni–0.8% Mo, and Cu–40% Ni–0.5% Nb alloys. It opens the prospect of using these alloys as epitaxial substrates in the technology of high-temperature second-generation superconductors. The evaluation of mechanical characteristics showed that alloying contributed to an increase in the yield strength of Cu–40% Ni–1.3% Mn, Cu–40% Ni–0.8% Mo, and Cu–40% Ni–0.5% Nb alloys by 3–4 times compared with the yield strength value of a textured copper band.