Determination of refractive index and absorbance modulation amplitudes from angular selectivity of holograms in polymer material with phenanthrenequinone

Amplitude and phase contributions to mixed volume holographic gratings were extracted from measured contours of angular selectivity. Holograms for the investigation were recorded in the glassy polymer material with phenan-threnequinone (PQ) using the DPSS CW laser (532 nm) and then self-developed due to molecular diffusion of PQ, reaching diffraction efficiency about 40%. Refractive index and absorbance modulation amplitudes of those holograms were obtained as adjustable parameters from theoretical equations by fitting angular dependencies of zeros and 1st orders diffraction efficiency measured at 450, 473, 532, and 633 nm at the different stages of hologram development. Mixed gratings manifest themselves in asymmetrical transmittance selectivity contours with one minimum and one maximum shifted with respect to the Bragg angle, while symmetrical contours with a minimum or a maximum at the Bragg angle are characteristic of pure phase and amplitude gratings, respectively. In the course of a hologram development, it converts from a predominantly amplitude-mixed to almost purely phase one in the case of readout using a light within the absorption band of PQ and maintains the phase nature besides it. The value of refractive index amplitude is ranging from 5×10-6 to 10-4 and the value of absorbance amplitude is up to 140 m-1.