{"title":"硼对气体渗碳低合金钢低周弯曲疲劳强度的影响","authors":"Ai Goto, Masato Yuya, Kaori Kawano","doi":"10.2355/tetsutohagane.tetsu-2023-092","DOIUrl":null,"url":null,"abstract":"The effect of boron addition on low cycle bending fatigue strength of carburized steel was investigated. The low-cycle bending fatigue strength of B-added steel was improved compared to SCM420. When the fatigue failure was divided into the crack initiation process and the crack propagation process, the addition of boron did not affect the crack initiation life, but improved the crack propagation life. The presence of boron in B-added steels was evaluated using TOF-SIMS and AES measurements. Grain boundary segregation of boron was not observed in the gas carburized surface layer, but precipitation of BN was observed. On the other hand, grain boundary segregation of boron was observed from the carburized surface layer toward the 400 μm core side. Therefore, it is considered that the grain boundary strengthening effect of boron was not obtained in the carburized surface layer, and the crack initiation life did not change.","PeriodicalId":22340,"journal":{"name":"Tetsu To Hagane-journal of The Iron and Steel Institute of Japan","volume":"17 1","pages":"0"},"PeriodicalIF":0.3000,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effects of Boron Addition on Low Cycle Bending Fatigue Strength of Gas Carburized Low Alloy Steel\",\"authors\":\"Ai Goto, Masato Yuya, Kaori Kawano\",\"doi\":\"10.2355/tetsutohagane.tetsu-2023-092\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The effect of boron addition on low cycle bending fatigue strength of carburized steel was investigated. The low-cycle bending fatigue strength of B-added steel was improved compared to SCM420. When the fatigue failure was divided into the crack initiation process and the crack propagation process, the addition of boron did not affect the crack initiation life, but improved the crack propagation life. The presence of boron in B-added steels was evaluated using TOF-SIMS and AES measurements. Grain boundary segregation of boron was not observed in the gas carburized surface layer, but precipitation of BN was observed. On the other hand, grain boundary segregation of boron was observed from the carburized surface layer toward the 400 μm core side. Therefore, it is considered that the grain boundary strengthening effect of boron was not obtained in the carburized surface layer, and the crack initiation life did not change.\",\"PeriodicalId\":22340,\"journal\":{\"name\":\"Tetsu To Hagane-journal of The Iron and Steel Institute of Japan\",\"volume\":\"17 1\",\"pages\":\"0\"},\"PeriodicalIF\":0.3000,\"publicationDate\":\"2023-01-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Tetsu To Hagane-journal of The Iron and Steel Institute of Japan\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.2355/tetsutohagane.tetsu-2023-092\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"METALLURGY & METALLURGICAL ENGINEERING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Tetsu To Hagane-journal of The Iron and Steel Institute of Japan","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.2355/tetsutohagane.tetsu-2023-092","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"METALLURGY & METALLURGICAL ENGINEERING","Score":null,"Total":0}
Effects of Boron Addition on Low Cycle Bending Fatigue Strength of Gas Carburized Low Alloy Steel
The effect of boron addition on low cycle bending fatigue strength of carburized steel was investigated. The low-cycle bending fatigue strength of B-added steel was improved compared to SCM420. When the fatigue failure was divided into the crack initiation process and the crack propagation process, the addition of boron did not affect the crack initiation life, but improved the crack propagation life. The presence of boron in B-added steels was evaluated using TOF-SIMS and AES measurements. Grain boundary segregation of boron was not observed in the gas carburized surface layer, but precipitation of BN was observed. On the other hand, grain boundary segregation of boron was observed from the carburized surface layer toward the 400 μm core side. Therefore, it is considered that the grain boundary strengthening effect of boron was not obtained in the carburized surface layer, and the crack initiation life did not change.
期刊介绍：
The journal ISIJ International first appeared in 1961 under the title Tetsu-to-Hagané Overseas. The title was changed in 1966 to Transactions of The Iron and Steel Institute of Japan and again in 1989 to the current ISIJ International.
The journal provides an international medium for the publication of fundamental and technological aspects of the properties, structure, characterization and modeling, processing, fabrication, and environmental issues of iron and steel, along with related engineering materials.
Classification
I Fundamentals of High Temperature Processes
II Ironmaking
III Steelmaking
IV Casting and Solidification
V Instrumentation, Control, and System Engineering
VI Chemical and Physical Analysis
VII Forming Processing and Thermomechanical Treatment
VIII Welding and Joining
IX Surface Treatment and Corrosion
X Transformations and Microstructures
XI Mechanical Properties
XII Physical Properties
XIII New Materials and Processes
XIV Social and Environmental Engineering.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们