Surface acoustic wave spectroscopy for non-destructive coating and bulk characterization at temperatures up to 600°C enabled by piezoelectric aluminum nitride coated sensor

Surface acoustic wave spectroscopy has been established as non-destructive and fast method for characterization of mechanical properties of surfaces and bulk materials in both research and industry. The present work shows that by application of a novel and robust aluminum nitride (AlN) coated piezoelectric contact sensor the advantages of the method can be extended from room temperature to at least 600°C. An overview of sensor concepts and applications of the method is discussed first, followed by theoretical and practical considerations for design and coating of a novel temperature stable contact sensor. After fabrication of such a sensor using magnetron sputtering, it was tested in a modified surface acoustic wave spectroscopy setup with an incorporated heating table concerning signal amplitude and frequency range. The AlN coated sensor was found to perform well up to 600°C, with temperature limited by the specification of the heating table. At room temperature, performance was acceptable when compared with a conventional contact sensor using a PVDF piezoelectric foil. Application of the high temperature capabilities of the setup was demonstrated by measuring temperature stability of hydrogen-free amorphous carbon coatings (a-C and ta-C) depending on their sp³ carbon ratio. In another example, high precision temperature dependent measurement of Young's modulus for ultrasonic fatigue test specimen was taken, achieving an accuracy better than 1%. Use of the developed sensor opens up new possibilities in material science for in situ study of temperature depending mechanical properties for coatings and surfaces.