Characterization and Self-Cleaning Properties of Silk Fabric Coated by Chitosan-Xyloglucan/nano-TiO2 Composite Film

In this study, Chitosan-Xyloglucan encapsulated Titanium dioxide was prepared by in-situ method for coating Silk fabric. FT-IR XRD characterized the functional groups and formation of crystallization of composite film. SEM analysis showed the immobilization of composite film on the surface of silk fabric. The coated silk fabrics were stained with methylene blue, and the stain removal efficiency was evaluated. The results showed that the composite film was deposited onto the silk fabric. The functional groups showed peaks around 1635 to 1636 and 400 to 500 cm-1 that indicate the presence of C=N groups of Chitosan-Xyloglucan and Ti-O groups of TiO2 on the composite, respectively. The XRD results indicated that the TiO2 prepared by the sol-gel method was an anatase crystalline structure. The mechanical properties showed the composite film was superior to the Chitosan-Xyloglucan, TiO2, and uncoated silk fabric. Finally, the methylene blue degradation capability was investigated. The coated silk fabric has insignificantly removing methylene blue stain than the untreated silk fabric, but it is noticeably repellent to stain.