A randomized controlled trial of immediate implant placement comparing hydroxyapatite nano-coated and uncoated sandblasted/acid-etched implants using a digital surgical guide.

Purpose: This study evaluated the implant stability, volumetric changes, and patient-reported outcome measures (PROMs) of hydroxyapatite (HA) nano-coated sandblasted/acid-etched (SLA) implants compared to uncoated SLA implants.

Methods: Forty patients were recruited and randomly allocated to HA nano-coated SLA group (test, n = 20) and uncoated SLA group (control, n = 20) using single-blinded/block randomization. Implants were immediately placed in maxillary posterior region using a digital surgical guide. Insertion torque and implant stability quotient (ISQ) were measured at implant surgery and 1, 2, 3, and 4 months postoperatively. Intraoral scans, PROMs and soft tissue inflammation data were collected, and multivariable linear regression analysis of ISQ was performed.

Results: In total, 48 implants (test; n = 24, control; n = 24) in 37 patients (test; n = 19, control; n = 18) were analyzed. Despite no significant between-group difference at surgery, the test group showed higher ISQ values than the control group at 2 (76.53 ± 4.17 vs. 71.32 ± 4.79, p < 0.01), 3 (77.45 ± 4.41 vs. 73.85 ± 4.69, p < 0.05), and 4 months (79.08 ± 2.96 vs. 73.43 ± 3.52, p < 0.0001) postoperatively. There were no significant differences in linear and volumetric changes, PROMs, and soft tissue inflammation analysis between two groups. The ISQ at implant surgery was influenced by age and diabetes mellitus (DM) at the implant level and DM and predicted total bone-to-implant contact area at the patient level.

Conclusion: HA nano-coated SLA implants promoted favorable immediate implants stability during early osseointegration phase compared to uncoated SLA implants, but displayed similar dimensional changes, PROMs, and soft tissue inflammation outcomes.

Trial registration: Clinical Research Information Service (CRIS), KCT0006364. Registered 21 July 2021, https://cris.nih.go.kr/cris/search/detailSearch.do?seq=24221&search_page=L .