{"title":"相组成和团簇结构对铸态和热处理 Ti33V37Mn30-xCrx 合金脱/水化动力学的影响","authors":"Bin Liu , Qiang Tao, Xiaoyu Chen","doi":"10.1016/j.intermet.2024.108398","DOIUrl":null,"url":null,"abstract":"<div><p>To enhance the hydrogen storage property, elements Mn in Ti<sub>33</sub>V<sub>37</sub>Mn<sub>30</sub> alloy were partially substituted with varying concentrations of elements Cr. The Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> variant, which exhibited superior performance, was selected for further analysis. Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> samples were first heat-treated separately at 773K, 973K and 1173K for 2h, and then water-quenched. The effect of Cr substitution and heat treatment on the microstructure and de-/hydriding properties of Ti<sub>33</sub>V<sub>37</sub>Mn<sub>30-<em>x</em></sub>Cr<sub><em>x</em></sub> alloys were investigated. As-cast alloys were composed of BCC phases mainly, along with some C14 Laves phases and Ti-rich phases. The lattice parameter of BCC phases in Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> increased to 3.053 Å. Cr substitution changed the tetrahedral gap of the alloy. At 298K, the initial hydrogen absorption capacity and the maximum hydrogen desorption capacity of Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> were raised to 3.07 wt% and 1.81 wt%, respectively. The lattice parameter of Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> alloys heat-treated at 773K also enlarged to 3.056 Å. Elevating the heat treatment temperature to 973K and 1173K significantly raised the proportion of C14 Laves phases in the alloy. Hydrogen storage performance of heat-treated alloys was examined at 298K. The results suggested that the heat-treated alloys could be fully activated after one hydrogen ab-/desorption cycle. Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> alloy heat-treated at 773K achieved the maximum hydrogen desorption capacity of 1.83 wt%, with an accelerated hydrogen ab-/desorption rate.</p></div>","PeriodicalId":331,"journal":{"name":"Intermetallics","volume":null,"pages":null},"PeriodicalIF":4.3000,"publicationDate":"2024-06-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Effect of phase composition and cluster structure on de-/hydriding kinetics of as-cast and heat-treated Ti33V37Mn30-xCrx alloys\",\"authors\":\"Bin Liu , Qiang Tao, Xiaoyu Chen\",\"doi\":\"10.1016/j.intermet.2024.108398\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>To enhance the hydrogen storage property, elements Mn in Ti<sub>33</sub>V<sub>37</sub>Mn<sub>30</sub> alloy were partially substituted with varying concentrations of elements Cr. The Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> variant, which exhibited superior performance, was selected for further analysis. Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> samples were first heat-treated separately at 773K, 973K and 1173K for 2h, and then water-quenched. The effect of Cr substitution and heat treatment on the microstructure and de-/hydriding properties of Ti<sub>33</sub>V<sub>37</sub>Mn<sub>30-<em>x</em></sub>Cr<sub><em>x</em></sub> alloys were investigated. As-cast alloys were composed of BCC phases mainly, along with some C14 Laves phases and Ti-rich phases. The lattice parameter of BCC phases in Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> increased to 3.053 Å. Cr substitution changed the tetrahedral gap of the alloy. At 298K, the initial hydrogen absorption capacity and the maximum hydrogen desorption capacity of Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> were raised to 3.07 wt% and 1.81 wt%, respectively. The lattice parameter of Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> alloys heat-treated at 773K also enlarged to 3.056 Å. Elevating the heat treatment temperature to 973K and 1173K significantly raised the proportion of C14 Laves phases in the alloy. Hydrogen storage performance of heat-treated alloys was examined at 298K. The results suggested that the heat-treated alloys could be fully activated after one hydrogen ab-/desorption cycle. Ti<sub>33</sub>V<sub>37</sub>Mn<sub>24</sub>Cr<sub>6</sub> alloy heat-treated at 773K achieved the maximum hydrogen desorption capacity of 1.83 wt%, with an accelerated hydrogen ab-/desorption rate.</p></div>\",\"PeriodicalId\":331,\"journal\":{\"name\":\"Intermetallics\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":4.3000,\"publicationDate\":\"2024-06-30\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Intermetallics\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0966979524002176\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"CHEMISTRY, PHYSICAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Intermetallics","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0966979524002176","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, PHYSICAL","Score":null,"Total":0}
Effect of phase composition and cluster structure on de-/hydriding kinetics of as-cast and heat-treated Ti33V37Mn30-xCrx alloys
To enhance the hydrogen storage property, elements Mn in Ti33V37Mn30 alloy were partially substituted with varying concentrations of elements Cr. The Ti33V37Mn24Cr6 variant, which exhibited superior performance, was selected for further analysis. Ti33V37Mn24Cr6 samples were first heat-treated separately at 773K, 973K and 1173K for 2h, and then water-quenched. The effect of Cr substitution and heat treatment on the microstructure and de-/hydriding properties of Ti33V37Mn30-xCrx alloys were investigated. As-cast alloys were composed of BCC phases mainly, along with some C14 Laves phases and Ti-rich phases. The lattice parameter of BCC phases in Ti33V37Mn24Cr6 increased to 3.053 Å. Cr substitution changed the tetrahedral gap of the alloy. At 298K, the initial hydrogen absorption capacity and the maximum hydrogen desorption capacity of Ti33V37Mn24Cr6 were raised to 3.07 wt% and 1.81 wt%, respectively. The lattice parameter of Ti33V37Mn24Cr6 alloys heat-treated at 773K also enlarged to 3.056 Å. Elevating the heat treatment temperature to 973K and 1173K significantly raised the proportion of C14 Laves phases in the alloy. Hydrogen storage performance of heat-treated alloys was examined at 298K. The results suggested that the heat-treated alloys could be fully activated after one hydrogen ab-/desorption cycle. Ti33V37Mn24Cr6 alloy heat-treated at 773K achieved the maximum hydrogen desorption capacity of 1.83 wt%, with an accelerated hydrogen ab-/desorption rate.
期刊介绍:
This journal is a platform for publishing innovative research and overviews for advancing our understanding of the structure, property, and functionality of complex metallic alloys, including intermetallics, metallic glasses, and high entropy alloys.
The journal reports the science and engineering of metallic materials in the following aspects:
Theories and experiments which address the relationship between property and structure in all length scales.
Physical modeling and numerical simulations which provide a comprehensive understanding of experimental observations.
Stimulated methodologies to characterize the structure and chemistry of materials that correlate the properties.
Technological applications resulting from the understanding of property-structure relationship in materials.
Novel and cutting-edge results warranting rapid communication.
The journal also publishes special issues on selected topics and overviews by invitation only.