模拟沿海储藏环境下 Mg-9Gd-3Y-2Zn-0.5Zr 合金中第二相的腐蚀行为

IF 6.6 2区 材料科学 Q1 MATERIALS SCIENCE, MULTIDISCIPLINARY npj Materials Degradation Pub Date : 2024-07-11 DOI:10.1038/s41529-024-00492-4
Junhang Chen, Chao Zhang, Zhihao Hu, Yao Tan, Shiwen Zou, Jin Gao, Xin Zhang, Kui Xiao
{"title":"模拟沿海储藏环境下 Mg-9Gd-3Y-2Zn-0.5Zr 合金中第二相的腐蚀行为","authors":"Junhang Chen, Chao Zhang, Zhihao Hu, Yao Tan, Shiwen Zou, Jin Gao, Xin Zhang, Kui Xiao","doi":"10.1038/s41529-024-00492-4","DOIUrl":null,"url":null,"abstract":"The Mg–9Gd–3Y–2Zn–0.5Zr alloy was studied for its long-term corrosion behavior in a simulated coastal storage environment. The results show that the Mg12 (Y, Gd) Zn phase in the Mg–9Gd–3Y–2Zn–0.5Zr alloy forms a galvanic couple with α-Mg, and the Mg12 (Y, Gd) Zn phase acts as a cathode to accelerate α-Mg during the corrosion initiation period. The corrosion of the anode is subsequently transformed into corrosive dissolution of the anode. With the dissolution of the Mg12 (Y, Gd) Zn phase, elements such as Gd and Y are gradually distributed into the entire corrosion product layer, improving the protective performance of the corrosion product layer by forming dense Gd2O3 and Y2O3.","PeriodicalId":19270,"journal":{"name":"npj Materials Degradation","volume":null,"pages":null},"PeriodicalIF":6.6000,"publicationDate":"2024-07-11","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.nature.com/articles/s41529-024-00492-4.pdf","citationCount":"0","resultStr":"{\"title\":\"Corrosion behavior of the second phase in Mg–9Gd–3Y–2Zn–0.5Zr alloy under simulated coastal storage environment\",\"authors\":\"Junhang Chen, Chao Zhang, Zhihao Hu, Yao Tan, Shiwen Zou, Jin Gao, Xin Zhang, Kui Xiao\",\"doi\":\"10.1038/s41529-024-00492-4\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The Mg–9Gd–3Y–2Zn–0.5Zr alloy was studied for its long-term corrosion behavior in a simulated coastal storage environment. The results show that the Mg12 (Y, Gd) Zn phase in the Mg–9Gd–3Y–2Zn–0.5Zr alloy forms a galvanic couple with α-Mg, and the Mg12 (Y, Gd) Zn phase acts as a cathode to accelerate α-Mg during the corrosion initiation period. The corrosion of the anode is subsequently transformed into corrosive dissolution of the anode. With the dissolution of the Mg12 (Y, Gd) Zn phase, elements such as Gd and Y are gradually distributed into the entire corrosion product layer, improving the protective performance of the corrosion product layer by forming dense Gd2O3 and Y2O3.\",\"PeriodicalId\":19270,\"journal\":{\"name\":\"npj Materials Degradation\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":6.6000,\"publicationDate\":\"2024-07-11\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.nature.com/articles/s41529-024-00492-4.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"npj Materials Degradation\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.nature.com/articles/s41529-024-00492-4\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"npj Materials Degradation","FirstCategoryId":"88","ListUrlMain":"https://www.nature.com/articles/s41529-024-00492-4","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

摘要

研究了 Mg-9Gd-3Y-2Zn-0.5Zr 合金在模拟沿海储存环境中的长期腐蚀行为。结果表明,Mg-9Gd-3Y-2Zn-0.5Zr 合金中的 Mg12 (Y, Gd) Zn 相与 α-Mg 形成电偶,Mg12 (Y, Gd) Zn 相作为阴极在腐蚀起始期加速了 α-Mg。阳极的腐蚀随后转化为阳极的腐蚀性溶解。随着 Mg12 (Y, Gd) Zn 相的溶解,Gd 和 Y 等元素逐渐分布到整个腐蚀产物层中,通过形成致密的 Gd2O3 和 Y2O3 提高了腐蚀产物层的保护性能。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

摘要图片

摘要图片

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Corrosion behavior of the second phase in Mg–9Gd–3Y–2Zn–0.5Zr alloy under simulated coastal storage environment
The Mg–9Gd–3Y–2Zn–0.5Zr alloy was studied for its long-term corrosion behavior in a simulated coastal storage environment. The results show that the Mg12 (Y, Gd) Zn phase in the Mg–9Gd–3Y–2Zn–0.5Zr alloy forms a galvanic couple with α-Mg, and the Mg12 (Y, Gd) Zn phase acts as a cathode to accelerate α-Mg during the corrosion initiation period. The corrosion of the anode is subsequently transformed into corrosive dissolution of the anode. With the dissolution of the Mg12 (Y, Gd) Zn phase, elements such as Gd and Y are gradually distributed into the entire corrosion product layer, improving the protective performance of the corrosion product layer by forming dense Gd2O3 and Y2O3.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
npj Materials Degradation
npj Materials Degradation MATERIALS SCIENCE, MULTIDISCIPLINARY-
CiteScore
7.80
自引率
7.80%
发文量
86
审稿时长
6 weeks
期刊介绍: npj Materials Degradation considers basic and applied research that explores all aspects of the degradation of metallic and non-metallic materials. The journal broadly defines ‘materials degradation’ as a reduction in the ability of a material to perform its task in-service as a result of environmental exposure. The journal covers a broad range of topics including but not limited to: -Degradation of metals, glasses, minerals, polymers, ceramics, cements and composites in natural and engineered environments, as a result of various stimuli -Computational and experimental studies of degradation mechanisms and kinetics -Characterization of degradation by traditional and emerging techniques -New approaches and technologies for enhancing resistance to degradation -Inspection and monitoring techniques for materials in-service, such as sensing technologies
期刊最新文献
Insights into the degradation mechanism of Fe-40Ni-15Co superalloy exposed to marine atmospheric and high-temperature conditions Lifetime prediction of epoxy coating using convolutional neural networks and post processing image recognition methods Film-forming amines as corrosion inhibitors: a state-of-the-art review The effect of variable humidity on corrosion fatigue of AA7085-T7451 with surface salt deposits Unveiling the mechanism behind irregular inclusions triggering no HIC cracks in steels
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1