不同厚度的 CAD/CAM 混合材料的透光性和遮色能力:体外研究。

IF 2.5 Q2 DENTISTRY, ORAL SURGERY & MEDICINE BDJ Open Pub Date : 2024-08-05 DOI:10.1038/s41405-024-00245-0
Zeinab Omar Tolba, Eman Ezzat Youssef Hassanien
{"title":"不同厚度的 CAD/CAM 混合材料的透光性和遮色能力:体外研究。","authors":"Zeinab Omar Tolba, Eman Ezzat Youssef Hassanien","doi":"10.1038/s41405-024-00245-0","DOIUrl":null,"url":null,"abstract":"<p><strong>Objective: </strong>To evaluate effect of material thickness and translucency of two different hybrid CAD/CAM materials on their masking ability.</p><p><strong>Materials and methods: </strong>40 rectangular-shaped specimens (12 × 14 mm) were obtained from Vita Enamic and Grandio blocks at 0.5 and 1 mm-thick (n = 10/group). Colour parameters of specimens were measured on PMMA tooth-coloured replica backgrounds (A2, C4) and black, white backings using dental spectrophotometer. Translucency parameter (TP) and masking ability (∆E<sub>00</sub>) values of tested materials with 0.5, and 1 mm thicknesses were calculated. Quantitative variables were compared between groups using student t-test.</p><p><strong>Results: </strong>TP and ∆E<sub>00</sub> significantly decreased as thickness of tested materials increased. Grandio showed significantly higher TP values. There were significantly lower ΔE<sub>00</sub> values for Vita Enamic compared to Grandio at 1 mm thickness and inversely insignificant at 0.5 mm. The 0.5 mm-thick ∆E<sub>00</sub> of tested materials was above clinical acceptability threshold, whereas, 1 mm-thick did not exceed showing better masking properties.</p><p><strong>Conclusions: </strong>Thickness is more effective for colour masking than translucency. In thin thickness, the masking ability is less effective, irrespective of tested materials. Translucency of tested materials was affected by their composition. Both hybrid CAD/CAM materials are promising alternatives for masking dark discolouration at 1 mm-thick.</p>","PeriodicalId":36997,"journal":{"name":"BDJ Open","volume":null,"pages":null},"PeriodicalIF":2.5000,"publicationDate":"2024-08-05","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.ncbi.nlm.nih.gov/pmc/articles/PMC11300448/pdf/","citationCount":"0","resultStr":"{\"title\":\"Translucency and colour masking ability of hybrid CAD/CAM materials with different thicknesses: in vitro study.\",\"authors\":\"Zeinab Omar Tolba, Eman Ezzat Youssef Hassanien\",\"doi\":\"10.1038/s41405-024-00245-0\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Objective: </strong>To evaluate effect of material thickness and translucency of two different hybrid CAD/CAM materials on their masking ability.</p><p><strong>Materials and methods: </strong>40 rectangular-shaped specimens (12 × 14 mm) were obtained from Vita Enamic and Grandio blocks at 0.5 and 1 mm-thick (n = 10/group). Colour parameters of specimens were measured on PMMA tooth-coloured replica backgrounds (A2, C4) and black, white backings using dental spectrophotometer. Translucency parameter (TP) and masking ability (∆E<sub>00</sub>) values of tested materials with 0.5, and 1 mm thicknesses were calculated. Quantitative variables were compared between groups using student t-test.</p><p><strong>Results: </strong>TP and ∆E<sub>00</sub> significantly decreased as thickness of tested materials increased. Grandio showed significantly higher TP values. There were significantly lower ΔE<sub>00</sub> values for Vita Enamic compared to Grandio at 1 mm thickness and inversely insignificant at 0.5 mm. The 0.5 mm-thick ∆E<sub>00</sub> of tested materials was above clinical acceptability threshold, whereas, 1 mm-thick did not exceed showing better masking properties.</p><p><strong>Conclusions: </strong>Thickness is more effective for colour masking than translucency. In thin thickness, the masking ability is less effective, irrespective of tested materials. Translucency of tested materials was affected by their composition. Both hybrid CAD/CAM materials are promising alternatives for masking dark discolouration at 1 mm-thick.</p>\",\"PeriodicalId\":36997,\"journal\":{\"name\":\"BDJ Open\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":2.5000,\"publicationDate\":\"2024-08-05\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.ncbi.nlm.nih.gov/pmc/articles/PMC11300448/pdf/\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"BDJ Open\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1038/s41405-024-00245-0\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q2\",\"JCRName\":\"DENTISTRY, ORAL SURGERY & MEDICINE\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"BDJ Open","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1038/s41405-024-00245-0","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"DENTISTRY, ORAL SURGERY & MEDICINE","Score":null,"Total":0}
引用次数: 0

摘要

目的:评估两种不同的混合 CAD/CAM 材料的厚度和半透明度对其遮盖能力的影响:评估两种不同的 CAD/CAM 混合材料的厚度和半透明度对其遮盖能力的影响。材料和方法:从厚度分别为 0.5 毫米和 1 毫米的 Vita Enamic 和 Grandio 块体中获得 40 个矩形试样(12 × 14 毫米)(n = 10/组)。使用牙科分光光度计在 PMMA 牙色复制品背景(A2、C4)和黑色、白色衬底上测量试样的颜色参数。计算厚度分别为 0.5 毫米和 1 毫米的受测材料的半透明参数 (TP) 值和遮蔽能力 (∆E00) 值。使用学生 t 检验比较各组之间的定量变量:结果:随着测试材料厚度的增加,TP 和 ∆E00 明显降低。Grandio 的 TP 值明显更高。在厚度为 1 毫米时,Vita Enamic 的 ΔE00 值明显低于 Grandio,而在厚度为 0.5 毫米时,两者的ΔE00 值不显著。测试材料 0.5 毫米厚度的ΔE00 值高于临床接受阈值,而 1 毫米厚度的ΔE00 值未超过临床接受阈值,显示出更好的遮盖特性:结论:厚度比半透明度更能有效遮盖颜色。结论:厚度比半透明度更能有效遮盖颜色,厚度越薄,遮盖能力越差,与测试材料无关。测试材料的半透明性受其成分的影响。这两种混合 CAD/CAM 材料都是掩蔽 1 毫米厚度深色变色的理想替代品。
本文章由计算机程序翻译,如有差异,请以英文原文为准。

摘要图片

查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Translucency and colour masking ability of hybrid CAD/CAM materials with different thicknesses: in vitro study.

Objective: To evaluate effect of material thickness and translucency of two different hybrid CAD/CAM materials on their masking ability.

Materials and methods: 40 rectangular-shaped specimens (12 × 14 mm) were obtained from Vita Enamic and Grandio blocks at 0.5 and 1 mm-thick (n = 10/group). Colour parameters of specimens were measured on PMMA tooth-coloured replica backgrounds (A2, C4) and black, white backings using dental spectrophotometer. Translucency parameter (TP) and masking ability (∆E00) values of tested materials with 0.5, and 1 mm thicknesses were calculated. Quantitative variables were compared between groups using student t-test.

Results: TP and ∆E00 significantly decreased as thickness of tested materials increased. Grandio showed significantly higher TP values. There were significantly lower ΔE00 values for Vita Enamic compared to Grandio at 1 mm thickness and inversely insignificant at 0.5 mm. The 0.5 mm-thick ∆E00 of tested materials was above clinical acceptability threshold, whereas, 1 mm-thick did not exceed showing better masking properties.

Conclusions: Thickness is more effective for colour masking than translucency. In thin thickness, the masking ability is less effective, irrespective of tested materials. Translucency of tested materials was affected by their composition. Both hybrid CAD/CAM materials are promising alternatives for masking dark discolouration at 1 mm-thick.

求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
BDJ Open
BDJ Open Dentistry-Dentistry (all)
CiteScore
3.70
自引率
3.30%
发文量
34
审稿时长
30 weeks
期刊最新文献
Evaluation of two different self-disinfection alginate impression material. Dental team barriers and enablers for the dental management of adults with severe obesity: a qualitative analysis. Mechanism of curcumin in the prevention and treatment of oral submucosal fibrosis and progress in clinical application research. Antibacterial and Cytotoxicity characteristics of experimental epoxy -based endodontic sealer loaded with silver gold nanoparticles: in vitro study. Beyond the Bite: Exploring Mental Health of Dental Faculty in Pakistan- a multi-institutional study.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1