IF 9.4 1区 材料科学 Q1 ENGINEERING, MECHANICAL International Journal of Plasticity Pub Date : 2024-08-08 DOI:10.1016/j.ijplas.2024.104086
{"title":"基于微结构演变与机械性能退化之间关系的蠕变疲劳损伤等级评估","authors":"","doi":"10.1016/j.ijplas.2024.104086","DOIUrl":null,"url":null,"abstract":"<div><p>Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of <span><math><msup><mi>γ</mi><mrow><mo>″</mo></mrow></msup></math></span> precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.</p></div>","PeriodicalId":340,"journal":{"name":"International Journal of Plasticity","volume":null,"pages":null},"PeriodicalIF":9.4000,"publicationDate":"2024-08-08","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S0749641924002134/pdfft?md5=f4a62d3a916b36eab7234de47caa2d64&pid=1-s2.0-S0749641924002134-main.pdf","citationCount":"0","resultStr":"{\"title\":\"Creep-fatigue damage level evaluation based on the relationship between microstructural evolution and mechanical property degradation\",\"authors\":\"\",\"doi\":\"10.1016/j.ijplas.2024.104086\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of <span><math><msup><mi>γ</mi><mrow><mo>″</mo></mrow></msup></math></span> precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.</p></div>\",\"PeriodicalId\":340,\"journal\":{\"name\":\"International Journal of Plasticity\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":9.4000,\"publicationDate\":\"2024-08-08\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.sciencedirect.com/science/article/pii/S0749641924002134/pdfft?md5=f4a62d3a916b36eab7234de47caa2d64&pid=1-s2.0-S0749641924002134-main.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"International Journal of Plasticity\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S0749641924002134\",\"RegionNum\":1,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"ENGINEERING, MECHANICAL\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"International Journal of Plasticity","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0749641924002134","RegionNum":1,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"ENGINEERING, MECHANICAL","Score":null,"Total":0}
引用次数: 0

摘要

蠕变-疲劳相互作用被认为是在高温下工作的部件的主要失效模式。随着工作时间的延长,这种相互作用不仅会改变材料的微观结构,还会引发机械性能的逐渐退化,对材料的变形和损伤行为产生重大影响。在这项工作中,通过定性表征阐明了 GH4169 超合金在蠕变疲劳过程中的动态微结构演变,随后通过将微结构退化与机械性能退化联系起来,开发了损伤程度评估方法。蠕变疲劳试验在 650 °C、不同拉伸保持时间下进行,并在寿命分数为 10%、50% 和 80% 时中断,以进行进一步分析和拉伸评估。结果表明,长时间暴露于保持时间下会导致γ″析出物变粗,同时低角度晶界增加,最终导致蠕变疲劳强度降低。空隙和裂纹的产生加剧了伸长率的下降,导致了一种包含晶间和跨晶开裂途径的混合断裂模式。综合微观结构演变对不同的退化程度进行定性分类,为损伤评估提供了可靠的物理基础。建立了一个映射模型,将平均核平均错向(微观降解指标)与拉伸塑性应变能量密度(宏观降解指标)相关联。利用该模型为损伤程度评估方法赋予了量化指标,并在 P92 钢中对其通用性进行了额外验证。这项研究深入探讨了材料蠕变疲劳诱导退化的定量损伤评估,从而为制定部件运行管理和检测计划提供了理论依据。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
查看原文
分享 分享
微信好友 朋友圈 QQ好友 复制链接
本刊更多论文
Creep-fatigue damage level evaluation based on the relationship between microstructural evolution and mechanical property degradation

Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of γ precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.

求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
International Journal of Plasticity
International Journal of Plasticity 工程技术-材料科学:综合
CiteScore
15.30
自引率
26.50%
发文量
256
审稿时长
46 days
期刊介绍: International Journal of Plasticity aims to present original research encompassing all facets of plastic deformation, damage, and fracture behavior in both isotropic and anisotropic solids. This includes exploring the thermodynamics of plasticity and fracture, continuum theory, and macroscopic as well as microscopic phenomena. Topics of interest span the plastic behavior of single crystals and polycrystalline metals, ceramics, rocks, soils, composites, nanocrystalline and microelectronics materials, shape memory alloys, ferroelectric ceramics, thin films, and polymers. Additionally, the journal covers plasticity aspects of failure and fracture mechanics. Contributions involving significant experimental, numerical, or theoretical advancements that enhance the understanding of the plastic behavior of solids are particularly valued. Papers addressing the modeling of finite nonlinear elastic deformation, bearing similarities to the modeling of plastic deformation, are also welcomed.
期刊最新文献
A variational framework for Cahn–Hilliard-type diffusion coupled with Allen–Cahn-type multi-phase transformations in elastic and dissipative solids Coupled cellular automata-crystal plasticity modeling of microstructure-sensitive damage and fracture behaviors in deformation of α-titanium sheets affected by grain size Tailoring multi-type nanoprecipitates in high-entropy alloys towards superior tensile properties at cryogenic temperatures Tailoring thickness debit for high-temperature fatigue resistance of Inconel 718 superalloy fabricated by laser powder bed fusion The dependence of Zener-Hollomon parameter on softening behavior and dynamic recrystallization mechanism of a biodegradable Zn-Cu-Mg alloy
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
现在去查看 取消
×
提示
确定
0
微信
客服QQ
Book学术公众号 扫码关注我们
反馈
×
意见反馈
请填写您的意见或建议
请填写您的手机或邮箱
已复制链接
已复制链接
快去分享给好友吧!
我知道了
×
扫码分享
扫码分享
Book学术官方微信
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术
文献互助 智能选刊 最新文献 互助须知 联系我们:info@booksci.cn
Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。
Copyright © 2023 Book学术 All rights reserved.
ghs 京公网安备 11010802042870号 京ICP备2023020795号-1