Study on the adsorption performance and regeneration of lignin-derived graphitic carbon for H2S

In pursuit of effective adsorption materials for malodorous gases such as H₂S and to broaden the utilization avenues of lignin waste, this study employed the direct pyrolysis method to synthesize three types of alkali lignin graphitized carbons, namely C-800, KC-700, and KEC-700. Among them, KEC-700 exhibits a high specific surface area of 1672.9 m²/g, significantly superior H₂S adsorption performance compared to other materials, an adsorption breakthrough time of up to 220 min, and a sulfur capacity of 67.1 mg/g. Structural analysis showed that the more oxygen-containing functional groups of lignin charcoal and the larger specific surface area facilitated the adsorption of H₂S. After reaching adsorption saturation, the degree of graphitization of lignin carbon diminishes. The H₂S adsorption products primarily manifest as elemental sulfur and sulfate within the pores of lignin carbon measuring less than 2 nm. Through thermal regeneration, the charcoal effectively eliminates the elemental sulfur adsorption product. Nevertheless, sulfate removal proved unsatisfactory, as the adsorption efficiency of KEC-700 following two thermal regenerations was approximately 41% of that observed for fresh samples.